研究了在1260℃烧结时,烧结时间对Ti-6Al-4V烧结坯力学性能的影响.结果表明:平均晶粒尺寸为45 μm的氢化-脱氢粉末样品在1 260C烧结3 h～6 h,其相对密度为95.6%～96.7%、拉伸强度648 MPa～686 MPa、屈服强度526 MPa～615 MPa,但延伸率仅小于4%.90%气雾化(晶粒尺寸为32.5 μm)和10%氢化-脱氢混合粉末样品在1 260℃烧结2 h～6 h,其相对密度大于95%、拉伸强度800 MPa～848 MPa、屈服强度712 MPa～762 MPa、延伸率7.4%～9.5%.混合粉末样品的力学性能几乎达到美国ASTM粉末冶金的标准.
Ti-6Al-4V compacts were fabricated by metal injection molding (MIM). Influence of vacuum sintering time on mechanical properties of the sintered compacts at 1260℃ were investigated. The experimental results show that the compacts sintered at 1 260℃ for 3 hours～6 hours, which was made from hydrogenation-dehydrogenation(HDH) powder(average particles size is 45 μm), had a relative density of 95.6%～ 96.7%, ultimate tensile strength (648 MPa～686 MPa) and 0.2% yield strength (526 MPa～615 MPa) but a lower elongation (＜4%) and that the compacts sintered at 1 260℃ for 2 hours～6 hours,which was made from 90wt% gas-atomized powder(average particles size is 32.5 μm) and 10 wt% HDH powder, had higher relative density (＞95%),ultimate tensile strength (800 MPa～848 MPa), 0.2% yield strength (712 MPa～762 MPa) and high elongation (7.4%～9.5%).The mechanical properties of mixed powder specimens were nearly equivalent to the ASTM for the PM compacts.
参考文献
| [1] | 罗国珍,周廉,邓炬.中国钛的研究和发展[J].稀有金属材料与工程,1997(05):1. |
| [2] | German R M.Advances in Powder Metallurgy and Particulate Materials-1990[M].Princeton:MPIF,1990:140. |
| [3] | Kei A;Yasunari K;Hiromichi I;Masaharu T .1989 A dyances in Powder Metallurgy-Volume3[Z].,1989. |
| [4] | Welsch G;Bunk W .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1982,13:889. |
| [5] | 蒲正利;张廷杰;李琳 .[J].稀有金属材料与工程,1996,25(04):25. |
| [6] | Wagoner Johnson A J;Bull C W et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2003,34A:295. |
| [7] | 姚泽坤,郭鸿镇,苏祖武,孙开本,徐永超,曹晓卿.热力参数对α+β两相钛合金再结晶百分数和力学性能的影响[J].稀有金属材料与工程,2000(05):340-343. |
| [8] | Liu Z;Welsch G .[J].Transactions A,1988,19A:527. |
| [9] | Smarsly W;Lee Y T;Welsch G .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1985,16:1831. |
| [10] | Moody N R;Garrison W M et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1993,24:161. |
| [11] | Terlinde G;Luetjering G .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1982,13:1283. |
| [12] | Liauo C S;Fu H C;Hsiao I C .[J].Materials Science and Engineering A,1999,271A:275. |
| [13] | Li Y G;Blenkinsop P A;Loretto M H et al.[J].Acta Matriallia,1999,47(10):2889. |
| [14] | CHRISTOPH LEYENS;MANFRED PETERS .Influence of Long-Term Annealing on Tensile Properties and Fracture of Near-#alpha# Titanium Alloy Ti-6A1-2.75Sn-4Zr-O.4Mo-0.45Si[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1996(6):1709-1717. |
| [15] | Daniel Eylon;Froes F H;Stanly Abkowitz.ASM Handbook (Vol. 7)-Powder Metal Technologies and Application[M].New York:ASM International Press,1998:874. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%