The surface of Ni61 Nb39 crystalline ingot was treated by laser surface melting with different processing parame-ters.A fully amorphous layer with a thickness of approximately 10 μm could be produced on the top surface under optimal parameters.An amorphous-crystalline composite layer with the depth from 10 to 50 μm,consisting of amor-phous matrix and intermetallic phases of Ni3 Nb and Ni6 Nb7 ,could be formed.The micro-hardness (about 831 HV) of the treated surface was remarkably improved by nearly 100% compared with the value of the crystalline substrate caused by the formation of the fully amorphous structure.A finite volume simulation was adopted to evaluate the temperature distribution in the laser-affected zone of Ni6 1 Nb3 9 alloys and to reveal the mechanism of glass formation in the laser-affected zone.