研究了TWIP钢(30Mn-3Si-3A1)在等径角挤压冷变形过程中的组织演变.结果表明,1道次变形后,产生大量10～40 nm宽的形变孪晶,同时出现的微观剪切带对孪晶进行了切割.随着道次的增加,孪生系统增多,形变孪晶相互交割.同时剪切带的数量增加,产生相互交错并切割孪晶板条.4道次变形后,组织变成由碎化带和割裂开的孪晶相互交织的变形结构.碎化部分超细晶晶粒尺寸为40～120 nm,而未碎化孪晶板条宽度降至5～20 nm.
The microstructure evolution of a TWIP steel during equal channel angular pressing(ECAP)was investi-gated experimentally.After one pass,a large number of deformation twins with band widths of 10-40 nm were produced.At the same time,these deformation twins were cut down by microshear bands.With increase of pressing passes,more twinning systems were activated and twin bands intersected each other.Also shear bands cut twinning bands and refine more area of microstructure.After 4 pressing passes,uhrafine grains with size of 40-120 nm were obtained.While several areas within which deformation twins were not cut down were distributed in the matrix of uhrafine grains.The width of these twin bands was decreased to 5-20 nm.
参考文献
| [1] | Valiev R Z;Langdon T G .Principles of Equal-Channel Angular Pressing as a Processing Tool for Grain Refinement[J].Progress in Materials Science,2006,51:881. |
| [2] | Iwahashi Y;Horita Z;Nemoto M .Equal-Channel Angular Pressing for the Processing of Superplastic Materials[J].Acta Materialia,1997,46(09):3317. |
| [3] | Grassel O.;Frommeyer G.;Meyer LW.;Kruger L. .High strength Fe-Mn-(Al, Si) TRIP/TWIP steels development - properties - application[J].International Journal of Plasticity,2000(10/11):1391-1409. |
| [4] | Sato K;Iehinose M;Hirotsu Y .Effects of Deformation In duced Phase Transformation and Twinning on the Mechanical Properties of Austenitic Fe-Mn-Al Alloys[J].ISIJ Interna tional,1989,29(10):868. |
| [5] | Frommeyer G;Brux U;Neumann P .Supra-Ductile and High-Strength Manganese-TRAP/TWlP Steels for High Energy Absorption Purposes[J].ISIJ International,2003,43(05):438. |
| [6] | lwahashi Y N;Wang J T;Horita Z J .Principle of Equal Channel Angular Pressing for the Processing of Ultrafine-GrainedMaterials[J].Scripta Materialia,1996,13:143. |
| [7] | Li Y S;Tao N R;Lu K .Microstructural Evolution and Nano-structure Formation in Copper During Dynamic Plastic Defor-mation at Cryogenic Temperatures[J].Acta Materialia,2008,57(01):230. |
| [8] | Huang CX;Gao YL;Yang G;Wu SD;Li GY;Li SX .Bulk nanocrystalline stainless steel fabricated by equal channel angular pressing[J].Journal of Materials Research,2006(7):1687-1692. |
| [9] | Zhang H W;Hei Z K;Liu G .Formation of Nanostructured Surface Layer on AISI 304 Stainless Steel by Means of Surface Mechanical Attrition Treatment[J].Acta Materialia,2003,52(04):1871. |
| [10] | Tao N R;Wu X L;Sui M L .Grain Refinement at the Nanoscale via Mechanical Twinning and Dislocation Interae-tion in a Nickel-Based Alloy[J].Journal of Materials Research,2004,19:1623. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%