以硫酸铝、氧氯化锆和氨水为原料,采用共沉淀法制备氧化铝-氧化锆复相陶瓷,借助XRD、SEM等手段对复相陶瓷进行表征,分析了微波烧结和常规烧结对陶瓷烧结体性能的影响.结果表明:微波烧结体的相对密度较常规烧结体的大,且随着烧结温度的升高烧结体的致密度增强,在1550℃可达99％以上;微波烧结体的最高抗弯强度为765 MPa.组分分析表明微波烧结体主要含m-ZrO2和α-Al2O3和少量t-ZrO2相,且晶粒分布均匀、微观组织致密.用微波烧结获得的材料显微结构较常规烧结有较大改善.
参考文献
| [1] | E. Salahi;H. Esfahani;I. Mobasherpour .Sintering behavior and mechanical properties of alumina/zirconia multilayers composite via nano-powder processing[J].CERAMICS INTERNATIONAL,2014(2):2717-2722. |
| [2] | Yuanlong Li;Hyoun-Ee Kim;Young-Hag Koh .Improving the surface hardness of zirconia toughened alumina (ZTA) composites by surface treatment with a boehmite sol[J].CERAMICS INTERNATIONAL,2012(4):2889-2892. |
| [3] | Heidy L. Calambas Pulgarin;Liliana B. Garrido;Maria P. Albano .Processing of different alumina-zirconia composites by slip casting[J].CERAMICS INTERNATIONAL,2013(6):6657-6667. |
| [4] | 白周喜,高如琴,周宁生,石凯,全建军.ZrO2含量对Al2O3/ZrO2复相陶瓷微观结构和力学性能的影响[J].硅酸盐通报,2013(08):1640-1644. |
| [5] | 刘志刚 .Al<,2>O<,3>/ZrO<,2>陶瓷复合材料的制备和强韧化机理研究[D].中国海洋大学,2009. |
| [6] | 刘振英,徐斌.烧结温度对刚玉斜锆石复相陶瓷粉体的性能影响[J].非金属矿,2013(03):10-12. |
| [7] | 饶平根,吴建青,叶建东,单爱党.添加氧化锆对氧化铝陶瓷的性能的影响[J].兵器材料科学与工程,2006(02):13-17. |
| [8] | 于庆华,王介强,郑少华,高新睿,王勇.液相沉淀法制备ZTA纳米复相陶瓷[J].复合材料学报,2006(03):108-113. |
| [9] | 黄红燕,邵忠财,王国营,艾红军.溶胶共沉淀法制备氧化锆氧化铝复合粉体[J].材料研究学报,2008(03):246-250. |
| [10] | 陈奕帆,卢冬梅,万乾炳,晋勇,朱居木.纳米氧化铝-氧化锆全瓷材料微波烧结的实验研究[J].华西口腔医学杂志,2006(01):73-76. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%