采用直流等离子体CVD法制备了金刚石膜,利用X射线衍射、光学显微镜、扫描电镜、激光拉曼光谱等技术研究了金刚石膜的微观组织,晶粒择优取向生长过程.结果表明:开始形核时,晶粒随机无择优生长;对基体表面氢刻蚀预处理,有利于晶胚形核长大.甲烷浓度对金刚石膜晶粒择优取向生长有重要影响:甲烷浓度较低时,金刚石膜(100)面择优生长,形成以(111)为主的八面体晶体,并且可以制取中心和边缘均匀、高质量光学级自支撑金刚石膜,但生长速率慢,效率低.同时也发现金刚石膜存在空位、孔洞等缺陷.
参考文献
[1] | Lee ST.;Peng HY.;Zhou XT.;Wang N.;Lee CS.;Bello I.;Lifshitz Y. .A nucleation site and mechanism leading to epitaxial growth of diamondfilms[J].Science,2000(5450):104-106. |
[2] | Chen Honwen;Victor Rudolph .[J].Diamond and Related Materials,2003,12(10-11):1633. |
[3] | 戴达煌;周克崧.金刚石薄膜沉积制备工艺与应用[M].北京:冶金工业出版社,2001:6. |
[4] | Lee W S;Bai Y J .[J].Thin Solid Films,2003,435(1-2):89. |
[5] | Almeida E C;Diniz A V;Rosolen J M et al.[J].Diamond and Related Materials,2005,14(3-7):679. |
[6] | 牛新平,王昕,马胜利,徐可为,刘维民.Graphit-ic与Dymon-ic薄膜的结构与性能研究[J].稀有金属材料与工程,2005(08):1291-1294. |
[7] | Zuo D W;Song S L;Xiang B K .[J].Key Engineering Materials,2004,258-259:517. |
[8] | Li D S;Zuo D W;Chen R F et al.[J].Key Engineering Materials,2006,315-316:385. |
[9] | Yamazato M;Higa A;Oshiro T .[J].Diamond and Related Materials,2006,15(4-8):917. |
[10] | 陈荣发,左敦稳,李多生,相炳坤,赵礼刚,王珉.甲烷浓度对等离子喷射金刚石厚膜生长稳定性的影响[J].金属学报,2005(10):1091-1094. |
[11] | 卢文壮,左敦稳,王珉,黎向锋,徐锋.Cr过渡层沉积粘附型CVD金刚石膜的机理研究[J].中国机械工程,2004(18):1676-1680. |
[12] | 安希忠,张禹,刘国权,秦湘阁,王辅忠,刘胜新.CVD金刚石膜{100}取向在改进化学反应模型下生长的原子尺度模拟[J].稀有金属材料与工程,2002(05):349-352. |
[13] | Kawarada H;Wild C;Hers N .[J].Applied Physics,1997,81(08):3490. |
[14] | Goodwin D G .[J].Journal of Applied Physics,1993,42(11):6890. |
[15] | 刘存业,刘畅.CVD金刚石膜的结构分析[J].物理学报,2003(06):1479-1483. |
[16] | Lang A R .[J].Journal of Crystal Growth,1977,42:625. |
[17] | 增泉.薄膜物理[M].北京:电子工业出版社,1991:329. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%