以化学共沉淀法制备的纳米TiO-Al复合粉体为原料,采用原位选择性氮化的方法制备了纳米TiN-Al复合粉体.应用化学热力学原理分析、计算了氮化反应的条件和机理,研究了氮化条件对氮化反应的影响.实验结果表明,氮化反应在700℃时开始进行,在900℃保温5h,氮化反应进行完全,TEM照片显示纳米TiN 颗粒均匀分布于Al3基体中,粒径为50~70um.

Nano TiN-Al2O3 composite powders were prepared by in-situ nitridation using nano TiO2-Al2O3 powders prepared by a coprecipitation method as starting
material. The nitridation conditions and mechanism were calculated and analyzed by using thermodynamic principle. The effect of nitridation reaction conditions
on nitridation reaction was studied. Experimental results show that the nitridation reaction begins at 700℃ and completes at 900℃ for 5h. TEM
micrographs show that nano TiN particles are dispersed into Al2O3 matrix. The size of nano TiN particles is about 50~70nm.

参考文献

[1] Niihara K. J. Ceram. Soc. Jpn., 1991, 99 (10): 974--982.
[2] Sternitzke M. J. Eur. Ceram. Soc., 1997, 17: 1061--1082.
[3] Stearns L C, Zhao J, Harmer M P. J. Eur. Ceram. Soc., 1992, 10: 448--453.
[4] 高濂,王宏志,洪金生(GAO Lian, et al). 无机材料学报(Journal of Inorganic Materials), 1999, 14(5): 795--799.
[5] Mukerji J, Biswas S K. J. Am. Ceram. Soc., 1990, 73: 142--145.
[6] Gogotsi Y G, Porz F. J. Am. Ceram. Soc., 1992, 78: 2251--2259.
[7] Bellosi A, De Porz G, Guicciardi S. J. Eur. Ceram. Soc., 1992, 10: 307--315.
[8] Tsugeki K, Kato T, Koyanagi Y, et al. J. Mater. Sci., 1993 28: 3168--3172.
[9] Kamiya K, Yoko T, Bessho M. J. Mater. Sci., 1987 22: 937--941.
[10] 梁英教,车萌昌. 无机物热力学数据手册. 沈阳: 东北大学出版社,1993年.