以过氧化二异丙苯(DCP)为引发剂,在双辊开炼机上采用马来酸酐(MAH)单体对顺丁橡胶(BR)进行接枝改性,通过红外光谱对其结构进行了表征;采用化学滴定法测定了反应产物中MAH的接枝率.接枝后的BR与丁腈橡胶(NBR)共混,制备了NBR/BR-g-MAH共混物,对共混物的力学性能、耐低温性能、热老化性能和耐油性能进行了测试和分析.结果表明,BR进行MAH接枝后,提高了NBR/BR-g-MAH共混物力学性能,提高了NBR低温性能,随着BR用量的增加,共混物料低温性能提高,但耐油性能下降,兼顾耐油性能和耐低温性能的最佳条件为m(NBR)∶m(BR-g-MAH)=85∶15.
参考文献
| [1] | J.-M. Degrange;M. Thomine;Ph. Kapsa;J. M. Pelletier;L. Chazeau;G. Vigier;G. Dudragne;L. Guerbe .Influence of viscoelasticity on the tribological behaviour of carbon black filled nitrile rubber (NBR) for lip seal application[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2005(1):684-692. |
| [2] | Tariq Yasin;Shamshad Ahmed;Fumio Yoshii;Keizo Makuuchi .Effect of acrylonitrile content on physical properties of electron beam irradiated acrylonitrile-butadiene rubber[J].Reactive & functional polymers,2003(issues 2/3):113-118. |
| [3] | J.Ziegler;R.H.Schuster .Influence of Silanization on Dynamic-Mechanical Properties and the Distribution of Silica in NBR/BR Blends[J].Kautschuk + Gummi, Kunststoffe,2008(10):510-517. |
| [4] | 李蒙,万昌瑞.并用BR改进NBR耐油、低温性能的研究[J].特种橡胶制品,2009(01):46-48. |
| [5] | 刘霞.硅烷化对NBR/BR共混体动态力学性能和白炭黑分散的影响[J].世界橡胶工业,2010(01):12-18. |
| [6] | 邱祖民,秦朝燕,曾芳.丁腈与顺丁并用胶在金属密封垫片的应用研究[J].南昌大学学报（工科版）,2012(03):205-208. |
| [7] | S. H. BOTROS;M. L. TAWFIC .Synthesis and Characteristics of MAH-g-EPDM Compatibilized EPDM/NBR Rubber Blends[J].Journal of Elastomers & Plastics,2006(4):349-365. |
| [8] | Tiwari, M;Noordermeer, JWM;Dierkes, WK;van Ooij, WJ .Effect of plasma polymerization on the performance of silica in NBR, EPDM and NBR/EPDM blends[J].Rubber Chemistry and Technology,2008(2):276-296. |
| [9] | 翁国文,张岩梅,黄秀秀,沈爱军,蔡七红,朱蓉.硫化体系对NBR压缩永久变形的影响[J].橡胶工业,2005(04):232-234. |
| [10] | 董智贤,周彦豪.马来酸酐接枝天然橡胶的制备及应用研究[J].弹性体,2010(02):10-15. |
| [11] | 李超,成煦,何其佳,张爱民.不同引发剂引发SBS接枝马来酸酐的机理研究[J].高分子学报,2002(06):813-817. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%