通过熔融共混等规聚丙烯(iPP)/邻苯二甲酸二丁酯(DBP)/邻苯二甲酸二辛酯(DOP)体系,采用热致相分离法(TIPS)制备iPP中空纤维膜,且在不同的拉伸温度及拉伸比下对中空纤维膜进行拉伸研究.对膜结构与透过性能进行了表征.采用环境扫描电子显微镜(SEM)对膜的内、外表面以及截面结构进行观测,发现拉伸后膜外表面的皮层以及膜结构得到有效改善.使用电子式万能试验机对中空纤维膜的拉伸强度进行了测试.随着拉伸温度和拉伸比的增加,膜的孔隙率、纯水通量以及拉伸强度均呈现先增大后减小的趋势.膜的孔隙率最大可提高35.3％,纯水通量提高了286.9％,拉伸强度可提高至6.86 MPa.nano-SiO2(纳米SiO2)添加的杂化膜经过拉伸后,孔隙率增大了46.8％,纯水通量提高了416.1％,拉伸强度提高了181.9％.研究表明:通过对iPP中空纤维膜进行拉伸处理,可以优化膜结构,并改善了膜表面皮层以及透过性能.
参考文献
| [1] | Castro A J .Method for making microporous product[P].US Pat:4247498,1980-01-07. |
| [2] | Tsai F;Torkelson J M .Microporous poly (methyl methacrylate) membranes:effect of a low viscosity solvent on the formation mechanism[J].Macromolecules,1990(23):4983-4989. |
| [3] | Lloyd D R;Kinzer K E;Tseng H S .Microporous membrane formation via thermally induced phase separation (Ⅰ) Solid liquid phase separation[J].Journal of Membrane Science,1990,52(03):239-261. |
| [4] | Lloyd D R;Kim S S;Kinzer K E .Microporous membrane formation via thermally-induced phase separation (Ⅱ) Liquid-liquid phase separation[J].Journal of Membrane Science,1991,64(1/2):1-11. |
| [5] | Matsuyama H.;Lloyd DR.;Berghmans S. .Formation of hydrophilic microporous membranes via thermally induced phase separation[J].Journal of Membrane Science,1998(2):213-224. |
| [6] | Matsuyama H.;Yamamoto A.;Yano H.;Maki T.;Teramoto M.;Mishima K. Matsuyama K. .Effect of organic solvents on membrane formation by phase separation with supercritical CO2[J].Journal of Membrane Science,2002(1/2):81-87. |
| [7] | P. van de Witte;P.J. Dijkstra;J.W.A. van den Berg;J. Feijen .Phase separation processes in polymer solutions in relation to membrane formation[J].Journal of Membrane Science,1996(1/2):1-31. |
| [8] | 镰田健资;南俊辅;吉田完尔 .多孔质ボリづロビ し ン中空丝及びその制造方法[P].日本特许公报,昭56-52123,1981. |
| [9] | 近藤瑞生;山本隆;福永修 .多孔质ボリづロビし ン中空丝の制造方法[P].日本特许公报,昭60-37201,1985. |
| [10] | 王学松.现代膜技术及其应用指南[M].北京:化学工业出版社,2005:117-121. |
| [11] | Kim J J;Jang T S;Y D Kwon .Structural study of microporous polypropylene hollow fiber membranes made by the melt-spinning and cold-stretching method[J].Journal of Membrane Science,1994,93(03):209-215. |
| [12] | Ryu J B;Song K;Kim S S .Preparation of chemical and fouling resistant semicrystalline membranes[J].Polymer-korea,2000,24(03):342-349. |
| [13] | XU Y;WANG S;MENG D .High mol.wt.membrane for kidney dialysis machine-is made from hollow polypropylene fibres and can be produced by low cost process[P].CN,1053373,1991-07-31. |
| [14] | 胡继文,黄勇,沈家瑞.聚丙烯中空纤维膜的微孔结构的控制[J].功能高分子学报,2002(01):24-28. |
| [15] | 胡继文,黄勇,沈家瑞.硬弹性聚丙烯中空纤维的形成[J].膜科学与技术,2002(05):21-24. |
| [16] | 顾斌,曹毅,杜强国,杨玉良.应力场下固-液相分离制备微孔聚丙烯中空纤维膜[J].功能高分子学报,1999(03):281-284. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%