采用X射线衍射分析(XRD)研究了Fe-Co-Nd-Dy-B非晶合金晶化过程中α-Fe、Fe3B纳米晶的生长动力学.根据纳米晶生长达到稳定状态所需的时间常数tE与退火温度Ta的关系,计算了α-Fe和Fe3B纳米晶的生长激活能为:Egα-Fe=95±2 kJ/mol和E Fe3B=133±13 kJ/mol.该值远小于α-Fe和Fe3B两相的表观晶化激活能:Ecα-Fe=555 kJ/mol和EcFe3B=481 kJ/mol.这表明Fe-Co-Nd-Dy-B非晶合金晶化过程中α-Fe和Fe3B纳米晶的形成主要由成核所控制.
参考文献
| [1] | Kneller E.F.;Hawig R. .The exchange-spring magnet: a new material principle for permanent magnets[J].IEEE Transactions on Magnetics,1991(4):3588-3560. |
| [2] | Schrefl T;Fidler J .Kronmüller H:Remanence and Coercivity in Isotropic Nanocrystalline Permanent Magnets[J].Physical Review B,1994,49(09):6100-6110. |
| [3] | Zhang HW.;Yan AR.;Sun ZG.;Shen BG.;Tung IC.;Chin TS.;Zhang WY. .The hard magnetic properties of nanocomposite Nd-3.6Pr5.4Fe83Co3B5 ribbons prepared by melt spinning[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(0):997-1000. |
| [4] | Zhang X Y;Zhang J W;Wang W K .Microstructure and Magnetic Properties of Sm2(Fe,Si)17Cx/α-Fe Nanocomposite Mangnets Prepared under High Pressure[J].Applied Physics Letters,1999,74(04):597-599. |
| [5] | X. Y. Zhang;Y. Guan;L. Yang;J. W. Zhang .Crystallographic texture and magnetic anisotropy of α-Fe/Nd_(2)Fe_(14)B nanocomposites prepared by controlled melt spinning[J].Applied physics letters,2001(15):2426-2428. |
| [6] | G.C. Hadjipanayis .Nanophase hard magnets[J].Journal of Magnetism and Magnetic Materials,1999(1/3):373-391. |
| [7] | McCormick PG.;Smith PAI.;Ding J.;Street R.;Miao WF. .Mechanically alloyed nanocomposite magnets (invited)[J].Journal of Applied Physics,1998(11 Pt.2):6256-6261. |
| [8] | 李伟,关颖,张湘义.Fe<,66.5>Co<,9.5>Nd<,3.5>Dy<,0.5>B<,20>非晶合金的晶化动力学研究[C].第十一届全国磁学和磁性材料会议论文集,2002:194-195. |
| [9] | Würschum R;Grupp C;Schaefer H -E .Simultaneous Study of Vacancy Formation and Migration at High Temper- atures in B2-Type Fe Aluminides[J].Physical Review Letters,1995,75(01):97-100. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%