采用异丙基黄原酸钠SIP、N-乙基-N-苯基二硫代氨基甲酸PX的复合促进剂体系（用量分别为1.5phhr和0.5phhr）可使天然橡胶/顺丁橡胶并用胶（并用比为70∶30）在90℃～95℃内快速硫化，硫化特性符合缓冲胶工艺的要求，但其性能与HG/T 4124-2009《预硫化缓冲胶》存在一定的差距。
Isopropyl xanthate sodium ( SIP) and N-Ethyl-N-phenyldithiocarbamic Acid Zinc Salt ( PX) ,1.5 and 0.5phhr respectively ,are applied to make up complex accelerator system ,and cause the NR/BR blends ( with a blending ratio of 70∶30 ) fast curing at 90℃~95℃.The vulcanization characteristics meet requirements of the cushion gum processing , but its performances keep a certain distance from those described in the HG /T 4124 -2009“precured tread cushion gum”.
参考文献
| [1] | 贾红兵;周宏斌 .偶联剂Si69对炭黑补强NR硫化胶性能的影响[J].,1998,45(09):532-535. |
| [2] | 叶文钦.谈预硫化翻胎胎体的保护[J].橡塑技术与装备,2008(08):14-16. |
| [3] | 高孝恒.翻新轮胎粘合缓冲胶性能的研究[J].橡胶科技市场,2009(23):16-21. |
| [4] | 高利,宋国君.有机蒙脱土对天然橡胶/顺丁橡胶纳米复合材料的增强及增容作用[J].合成橡胶工业,2010(05):378-381. |
| [5] | 严志云,宁凯军,姜其斌,刘安华,贾德民.NR/BR/NBR并用胶的结构与性能[J].橡胶工业,2003(07):389-392. |
| [6] | 王进文.黄原酸盐促进剂在异丁烯类弹性体硫化中的应用[J].世界橡胶工业,2009(06):8-18. |
| [7] | 余广华.翻新轮胎超低温粘合胶配方技术及制备工艺研究与应用[J].中国轮胎资源综合利用,2010(07):21-26. |
| [8] | 宋国君,高利,李培耀,谷正,李汉华,单春鹏,杨晓宇.NR/BR/OMMT纳米复合材料的结构与性能研究及其在轮胎胎面胶中的应用[J].现代化工,2010(01):60-62. |
| [9] | 黄琛,范汝良,张勇,张隐西.NR硫化返原过程的动力学研究[J].橡胶工业,2000(04):195-200. |
| [10] | 庄文媛;赵月薇;范桂敏 .NR-BR/EPDM 并用胶硫化的研究[J].合成橡胶工业,1993,16(06):359-362. |
| [11] | 傅万森;于立明;刘宗伟 等.BR/NR 并用导电橡胶配方设计[J].橡胶工业,1997,44(11):661-663. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%