利用金相显微镜及SEM研究了在单向热锻拔长的工艺下,锻造比的不同对H13电炉钢组织和力学性能的影响。结果表明：同一锻造比下H13电炉钢的横向冲击功明显小于纵向,且无论在钢锭的横向、纵向边部到心部的冲击功越来越差;不同的锻造比对横向冲击功影响不大,而随着锻造比的增大纵向冲击功增大。研究表明,单向热锻拔长不能有效地提高钢材横向止裂性能;电炉H13热作模具钢的锻造比控制在4～6的范围内较为合适。
Effect of different forging ratios on microstructure and mechanical properties of electrical die steel（H13） was investigated by metallographic microscope and SEM under simplex stretching and hot-forging condition.The results show that transversal impact property is much less than longitudinal in the same forging ratio.Following the forging ratio increasing,it makes merely influence on the transversal impact property,while the longitudinal impact property increases.The research shows that,the cross direction crack arrest property won＇t be effectively influenced by forging ratio under simplex stretching and hot-forging condition.The forging ratio of electrical hot die steel should be controlled in four to six,which is most appropriate.
参考文献
| [1] | 陈再枝;蓝德年.模具钢手册[M].北京:冶金工业出版社,2002 |
| [2] | 霍晓阳.影响H13热作模具钢等向性的因素[J].钢铁研究学报,2008(11):47-50,54. |
| [3] | 章洪涛.铌钢和铌合金[A].北京:冶金工业出版社,2000 |
| [4] | 杨王玥,胡安民,孙祖庆.低碳钢奥氏体晶粒尺寸的控制[J].金属学报,2000(10):1050-1054. |
| [5] | 刘云旭.低碳合金钢中带状组织的成因、危害和消除[J].金属热处理,2000(12):1-3. |
| [6] | 邹安全,邓芬燕,邓沛然.等温球化退火对H13钢组织和性能的影响[J].金属热处理,2003(08):34-35. |
| [7] | 田玉新,蔡海燕,支玉明,陆明和,殷光虹.影响H13芯棒钢冲击韧性的因素分析[J].宝钢技术,2009(05):22-26. |
| [8] | 杨卫国 .热作模具钢显微组织新的评级图谱[J].国外金属热处理,2000,21(04):17. |
| [9] | Corwyn,Berger M;John Finn.The effect of Annealed Micro structure on the Impact Toughness of Premium H 13 Die Steel[A].Indiana,U.S.A,1995 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%