A single forming equipment of bimetal continuous core-filling casting was designed and manufactured for the purpose of developing copper-aluminum composite materials. The characteristics of the equipment were as follows: the crystallizer composed of water jacket copper sleeve in which graphite sleeve was set, two melting furnaces with different diameters vertically distributed, the low furnace of melting copper linked with the crystallizer, continuous casting and core-filling proceeded at the meantime. The rational processing parameters were determined through a series of experiments: contact length from down crucible to water-cooling cupreous crystallizer, 20~mm; length of recooling spray jet under crystallizer, 95~mm; temperature of copper and aluminum, 1250-1320 ℃ and 700 ℃ respectively; pulling rate, 16 mm/min. The qualified copper-clad aluminum composite rods, the external and inner diameter of which was 40~mm and 2 mm respectively, could be drawn successfully on that basis. Tested by hydrostatic extrusion and drawing process, the boss ratios of the copper-clad aluminum composite rods were maintained a relatively stable scope of about 0.59--0.65, which was not obviously changed by subsequent plastic processing.

参考文献

[1]
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%