通过金相分析、扫描电镜、能谱分析,同时结合热力学及动力学计算的方法,对Ni-22Cr-12Co镍基高温合金电渣重熔TiN变化行为进行研究,结果表明:在试验条件下,真空锭和电渣锭中的夹杂物均为以Al2O3为核心的TiN夹杂物;电渣重熔过程中,计算所得TiN回溶时间为1.17s;电渣重熔对去除TiN夹杂物几乎不起作用;计算所得TiN析出尺寸约为5μm,略小于试验值.

参考文献

[1] Viswanathan R;Henry J F;Tanzosh J et al.U.S.Progra mon Materials Technology for Ultra-Supercritical Coal Power Plants[J].Journal of Materials Engineering and Performance,2005,14(02):281.
[2] Christopher J. Cowen;Paul E. Danielson;Paul D. Jablonski .The Microstructural Evolution of Inconel Alloy 740 During Solution Treatment, Aging, and Exposure at 760℃[J].Journal of Materials Engineering and Performance,2011(6):1078-1083.
[3] Viswanathan R;Coleman K;Rao U .Materials For UltraSupercritical Coal-Fired Power Palnt Boilers[J].International Journal of Pressure Vessels and Piping,2006,83(11-12):778.
[4] 谢锡善,赵双群,董建新,张麦仓.超超临界电站用Inconel 740镍基合金的组织稳定性及其改型研究[J].动力工程学报,2011(08):638-643.
[5] Zhao Shuangqun;Xie Xishan;Smith G D et al.Microstructure Stability and Mechanical Properties of a New NickelBased Superalloy[J].Materials Science and Engineering,2003,A355:96.
[6] Shuangqun Zhao;Xishan Xie;Gaylord D. Smith .Gamma prime coarsening and age-hardening behaviors in a new nickel base superalloy[J].Materials Letters,2004(11):1784-1787.
[7] N.D. Evans;P.J. Maziasz;R.W. Swindeman .Microstructure and phase stability In INCONEL alloy 740 during creep[J].Scripta materialia,2004(6):503-507.
[8] 赵双群,董建新,张麦仓,谢锡善.新型镍基高温合金在950℃和1000℃的氧化行为[J].稀有金属材料与工程,2005(02):208-211.
[9] 李正邦.电渣冶金的理论与实践[M].北京:冶金工业出版社,2010
[10] 傅杰;朱觉 .电渣重熔过程中氧化物夹杂的变化[J].金属学报,1964,7(03):250.
[11] 傅杰.特种熔炼与冶金质量控制[M].北京:冶金工业出版社,1999
[12] 陈家祥.炼钢常用图标数据手册[M].北京:冶金工业出版社,2010
[13] 格里古良BA;曲英.炼钢过程的物理化学计算[M].北京:冶金工业出版社,1993
[14] 闵志先,沈军,冯周荣,王灵水,刘林,傅恒志.定向凝固DZ125合金的溶质分配系数及偏析行为的研究[J].金属学报,2010(12):1543-1548.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%