本论文采用注射成型技术制备氧化锆增韧氧化铝(ZTA)陶瓷,系统分析了粉末固含量对注射成型喂料流变性能及陶瓷坯体的烧结和力学性能的影响.结果表明:随着粉末固含量的增加,喂料的粘度和非牛顿指数都有所增加,尤其当固含量达到65vol%时,喂料的粘度急剧增大;注射生坯的密度也随着固含量增加有所提高,但烧结收缩率反而相应降低了,特别是65vol%固含量时,烧结收缩率明显下降,这是由于坯体内存在较大的无法排除的气孔缺陷,所以导致最终烧结坯体的密度只略微增加;坯体的抗弯强度随着固含量增加到60vol%时达到最大.综上,喂料中60vol%粉末固含量是最适宜ZTA陶瓷注射成型工艺的.
参考文献
[1] | 李悦彤,杨静.氧化铝陶瓷低温烧结助剂的研究进展[J].硅酸盐通报,2011(06):1328-1332. |
[2] | 吴锋,李志坚,霍琳,曲殿利,唐建平,李心慰,徐娜.ZrO2和TiO2对刚玉质陶瓷蓄热体热震稳定性的影响[J].硅酸盐通报,2011(03):550-553. |
[3] | D. Casellas;M. M. Nagl;L. Llanes .Fracture toughness of alumina and ZTA ceramics: microstructural coarsening effects[J].Journal of Materials Processing Technology,2003(0):148-152. |
[4] | N. Schlechtriemen;J.R. Binder;R. Knitter .Optimization of feedstock properties for reaction-bonded net-shape zircon ceramics by design of experiments[J].CERAMICS INTERNATIONAL,2010(1):223-229. |
[5] | Wei Liu;Zhipeng Xie;Tiezhu Bo .Injection molding of surface modified powders with high solid loadings: A case for fabrication of translucent alumina ceramics[J].Journal of the European Ceramic Society,2011(9):1611-1617. |
[6] | T. Hanemann .Influence of particle properties on the viscosity of polymer-alumina composites[J].CERAMICS INTERNATIONAL,2008(8):2099-2105. |
[7] | Dean-Mo Liu;Wenjea J. Tseng .Influence of powder agglomerates on the structure and rheological behavior of injection-molded zirconia-wax suspensions[J].Journal of the American Ceramic Society,1999(10):2647-2652. |
[8] | Anne Mannschatz;Axel Muller;Tassilo Moritz .Influence of powder morphology on properties of ceramic injection moulding feedstocks[J].Journal of the European Ceramic Society,2011(14):2551-2558. |
[9] | M.E. Sotomayor;A. Varez, B. Levenfeld .Influence of powder particle size distribution on rheological properties of 316 L powder injection moulding feedstocks[J].Powder Technology: An International Journal on the Science and Technology of Wet and Dry Particulate Systems,2010(1/2):30-36. |
[10] | P. Thomas-Vielma;A. Cervera;B. Levenfeld .Production of alumina parts by powder injection molding with a binder system based on high density polyethylene[J].Journal of the European Ceramic Society,2008(4):763-771. |
[11] | Z.-p. Xie;J.-s. Luo;X. Wang .The effect of organic vehicle on the injection molding of ultra-fine zirconia powders[J].Materials & Design,2005(1):79-82. |
[12] | Birgit Loebbecke;Regina Knitter;Jurgen HauBelt .Rheological properties of alumina feedstocks for the low-pressure injection moulding process[J].Journal of the European Ceramic Society,2009(9):1595-1602. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%