ON THE AB_3 TYPE ALLOY PHASES OF(Nd, Gd. Dy)-Ir SYSTEM

CHEN Nianyi , XU Hua , YANG Chuanzheng(Shanghai Institute of Metallurgy , Academia Sinica) NING Yuantao , ZHENG Yun(Institute of Precious Metals

<正> 用计算机模式识别方法预测未知的合金中间相,是一种很有效的方法。用元素的价电子数Z、金属半径R、功函数φ等的函数张成多维空间,将已知金属间化合物绘入空间,用上述方法可以区分各种晶型的分布区域。据此可预报未知的合金中间相。我

Some empirical rules governing the crystal type of AB_3 type alloy phases have been obtained by pattern recognition method. By computerized prediction, we have predicted that Dy-Ir, Gd-Ir and Nd-Ir systems form AuCu_3 type alloy phases. Based on this prediction, we have prepared Dy-Ir, Gd-Ir and Nd-Ir alloy samples and haste proved the existence of DyIr_3, GdIr_3 and NdIr_3 alloy phases, with AuCu_3 structure Their lattice parameters are: a=0.3842nm, a=0.3839nm and a=03836nm respectively.

参考文献

[1]
[2]
[3]
[4]
[5]
[6]
[7]

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网