Effect of 0.1 wt pct Dy addition on microstructure and compressive behavior of NiAl-28Cr-5.8Mo-0.2 Hf eutectic alloy was investigated. The results showed that remarkable lamellar refinement can be achieved with the addition of 0.1 wt pct Dy. The Dy addition results in the decrease in Young's modulus of alloy and the. enhancement of the compressive strength and ductility of alloy at all testing temperatures. The lamellar refinement, the increased dislocation networks located at the interfaces of NiAl/Cr(Mo) and the strengthening of cell boundary are benefical to the improvement of compressive properties of the alloy.
参考文献
| [1] | D B Miracle .[J].Acta Materialia,1993,41:649. |
| [2] | R D Noebe;R R Bowman;M V Nathal .[J].International Materials Reviews,1993,38:193. |
| [3] | Jianting GUO.Ordered Intermetallic Compound NiAl Alloy[M].北京:科学出版社,2003 |
| [4] | D R Johnson;X F Chen;B F Oliver;R D Noebe, J D Whittenberger .[J].Intermetallics,1995,3:99. |
| [5] | J M Yang;S M Jeng;K Bain;R A Amato .[J].Acta Materialia,1996,45(01):295. |
| [6] | Q. Gao;J. T. Guo;K. W. Huai .The microstructure and compressive properties of as-cast NiAl-28Cr-5.8Mo-0.2Hf containing minor Dy[J].Materials Letters,2005(23):2859-2862. |
| [7] | K A Jackson;J D Hunt .[J].Transactions of the Metallurgical Society of AIME,1966,236:1129. |
| [8] | J S Pan;J M Tong;M B Tian.Int.Mater.Sci[M].北京:清华大学出版社,1998 |
| [9] | W L Ren;J T Guo;J Y Zhou .[J].Journal of Rare Earths,2002,20(04):295. |
| [10] | W L Ren;J T Guo;G S Li;J Y Zhou .[J].Materials Letters,2003,57:137. |
| [11] | J L Walter;H E Cline .[J].Metallurgical and Materials Transactions,1970,1:1221. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%