为抑制碳钢酸洗时的腐蚀,采用加热回流萃取法从薄荷叶中提取了一种新型绿色缓蚀剂.采用失重法和极化曲线法测试了薄荷叶缓蚀剂在20～ 50℃时对2 mol/L HC1中热轧碳钢的缓蚀性能.结果表明:薄荷叶缓蚀剂对热轧碳钢的缓蚀效率随其浓度增加而增大,最大缓蚀率达到87.8％;当浓度小于80 mg/L时,温度升高,缓蚀效率减小;浓度大于80 mg/L时,温度升高,缓蚀效率增大;薄荷叶缓蚀剂在热轧碳钢表面的吸附作用符合Lang-muir吸附模型;薄荷叶缓蚀剂对热轧碳钢的缓蚀机理为几何覆盖效应,同时抑制腐蚀反应的阴、阳极过程,属于混合型缓蚀剂.
参考文献
| [1] | 张天胜;张浩;高红.缓蚀剂[M].北京:化学工业出版社,2008:1-11. |
| [2] | 吴振兴 .金属基材腐蚀抑制剂的合成及性能的研究[D].北京工业大学,2009. |
| [3] | P.C. Okafor;C;Okafor;M.E. Ikpi;E;Ikpi;I.E. Uwah;E;Uwah;E.E. Ebenso;E;Ebenso;U.J. Ekpe;J;Ekpe;S.A. Umoren;A;Umoren .Inhibitory Action Of Phyllanthus Amarus Extracts On The Corrosion Of Mild Steel In Acidic Media[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(8):2310-2317. |
| [4] | Saleh R M;Ismail A A;El-Hosary A A .Corrosion Inhibition by Naturally Occurring Substances.Ⅶ.The Effect of Aqueous Extracts of Some Leaves and Fruit Peels on the Corrosion of Steel,Aluminum,Zinc and Copper in Acids[J].British Corrosion Journal,1982,17:131-135. |
| [5] | 梁振益,吴娟.薄荷提取物抗氧化性能的研究[J].中国油脂,2008(02):26-28. |
| [6] | 郭学辉,王康,胡百顺,石茂才,周生杰,余海棠.氨基酸类缓蚀剂缓蚀机理研究进展[J].腐蚀科学与防护技术,2013(01):63-66. |
| [7] | 邱贺媛,章宋洁.薄荷叶中黄酮类物质的提取及其抗氧化活性研究[J].安徽农业科学,2010(34):19335-19337,19340. |
| [8] | 陈秋林 .中药薄荷草的化学成分分析研究[D].南京工业大学,2004. |
| [9] | 胡思行,和鹏竹,周晓荣.柚子皮提取物对热轧碳钢在HCl溶液中的缓蚀作用研究[J].表面技术,2012(06):30-32,87. |
| [10] | 李晓燕.食品检测[M].北京:化学工业出版社,2011:125. |
| [11] | 孟令芝;龚淑玲;何永炳.有机波谱分析[M].武汉:武汉大学出版社,2003:233. |
| [12] | Eugenio A. Flores;Octavio Olivares;Natalya V. Likhanova;Marco A. Domfnguez-Aguilar;Noel Nava;Diego Guzman-Lucero;Monica Corrales .Sodium phthalamates as corrosion inhibitors for carbon steel in aqueous hydrochloric acid solution[J].Corrosion Science,2011(12):3899-3913. |
| [13] | 王星 .酸性体系中金属的缓蚀剂研究[D].武汉:武汉工业学院,2012. |
| [14] | 朱一帆,万小山.AMT在碳钢-5%HCl体系中的缓蚀行为及其机理研究[J].腐蚀科学与防护技术,1998(06):331. |
| [15] | 郑兴文,龚敏,王莹,姜春梅.甲硫氨酸对碳钢在硫酸介质中的缓蚀作用[J].化学研究与应用,2011(12):1589-1594. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%