CCT curves of Mn-Si steels with different manganese contents or carbon contents were determined. The results show that the transformation range of bainite can be separated from that of ferrite when the manganese content approaches a certain content, and the incubation period of ferrite increases more significantly than that of bainite transformation with the increase of carbon content in Mn-Si steels. Furthermore, water-cooled bainitic steels without adding expensive alloying element were developed. Granular bainite was obtained when a bar with diameter of 300 mm was cooled by water, and a mixed microstructure of granular bainite and martensite was obtained in water-cooled plate with thickness of 40 mm. The developed water-cooled bainitic steels containing no expensive alloying element showed a good combination of strength and toughness. The tensile strength, yield strength, and toughness (A_(KU) at -20 ℃) of bar with diameter of 300mm after water cooling were higher than 850 Mpa, 620 Mpa, and 65 J, respectively, and those of plate with thickness of 40mm after water cooling were higher than 1000 Mpa, 800 Mpa, and 50J, respectively.
参考文献
| [1] | FANG Hong-sheng .Novel Hot Rolling Bainitic Steel-Low Carbon Mn-B Series Engineering Steels 12Mn-B and 16Mn-B[J].Metallic Materials Research,1976,4(12):913. |
| [2] | YANG Liu;FANG Hong-sheng;MENG Zhi-he .Kinetics of Austenitic Isothermal Decomposition and Mn Partition in Fe-C-Mn-B Alloys[J].Acta Metallurgica Sinica,1992,28(01):A16. |
| [3] | 方鸿生,冯春,郑燕康,杨志刚,白秉哲.新型Mn系空冷贝氏体钢的创制与发展[J].热处理,2008(03):2-19. |
| [4] | YANG Zhi-gang;FANG Hong-sheng;WANG Jia-jun et al.Study of the Novel Carbon Mn-B Bainitic Steel Auto Connecting Rod and Freight Fork[J].Materials for Mechanical Engineering,1993,17(06):18. |
| [5] | 方鸿生,刘东雨,常开地,张弛,顾家琳,张文征,白秉哲,杨志刚.1 500 MPa级经济型贝氏体/马氏体复相钢的组织与性能[J].钢铁研究学报,2001(03):31-36. |
| [6] | HUANG Wei-gang;FANG Hong-sheng;ZHENG Yan-kang .Effect of Silicon Content on the Microstructure and Properties in Mn-B Air-Cooled Bainitic Steel[J].Transactions of Materials and Heat Treatment,1997,18(01):8. |
| [7] | ZHANG Ming-xing;KANG Mo-kuang .Influence of Si on Microstructure and Properties of Low Carbon Bainitic Steels[J].Acta Metallurgica Sinica,1993,29(01):A6. |
| [8] | LIU Shi-kai;YANG Liu;ZHANG Jun et al.Influence of Si and Mn on Morphology of Bainitic Ferrite and Kinetics of Bain-ite Transformation in Fe-C alloy[J].Acta Metallurgica Sinica,1992,28(12):A513. |
| [9] | 王凤香,简方,冯岩.27SiMn钢CCT曲线的测定[J].包钢科技,2007(02):26-29. |
| [10] | 肖桂枝,邸洪双,贾学军.热处理工艺对30MnSi PC钢棒力学性能的影响[J].钢铁,2007(04):73-77. |
| [11] | 冯岩,王凤香,简方.27SiMn液压支柱管组织演变规律的实验研究[J].包钢科技,2006(01):32-35. |
| [12] | 李安铭.奥氏体化温度和时间对27SiMn钢组织和性能的影响[J].金属热处理,2003(09):39-41. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%