基于微观相场动力学模型,研究沉淀早期不同成分Ni-Al-V合金时效时有序相的生长和组织生长方向的变化.结果表明:沉淀早期有序相间的竞争生长会很大程度地影响合金的形貌及生长方向.在一定的温度、应力场作用下,Al含量较低时,DO22有序相先析出,DO22相颗粒数量较多、尺寸较小,有序相的筏化不明显,合金整体上无显著的筏化现象；Al含量稍高时,L12相先析出,DO22相颗粒数量较少、尺寸较大,组织在[010]方向上发生一定程度的择优生长；Al含量较高时,L12相先析出,DO22相颗粒数量继续减少、尺寸继续增大,组织在[100]方向上显示出较强的筏化趋势；较低温度时效的合金L12有序相析出提前,组织的筏化趋势较弱.
参考文献
| [1] | Stallybrass C;Schneider A;Sauthoff G .[J].Intermetallics,2005,13:1263. |
| [2] | Socrate S;Parks D M .[J].Acta Metallurgica Et Materialia,1993,41:2185. |
| [3] | Tomihisa K;Kanenoand Y et al.[J].Intermetallics,2004,12:317. |
| [4] | Tian Sugui;Zhang Jinghua;Yang Hongcai .[J].Acta Metallurgica Sinica,1998,34(06):591. |
| [5] | Peng Zhifang;Yan Yanhui .[J].Acta Metallurgica Sinica,1997,33(11):1147. |
| [6] | Lapin J .[J].Intermetallics,2006,14:1417. |
| [7] | Poduri R;Chen L Q .[J].Acta Materialia,1998,46(11):3915. |
| [8] | Zhu J Z;Chen L Q;Shen J.[J].Modelling and Simulation in Materials Science and Engineering,2001(09):499. |
| [9] | Poduri R;ChenL Q .[J].Acta Materialia,1996,44(10):4253. |
| [10] | Zhao Y H;Chen Z .[J].Chinese Journal of Rare Metals,2003,27(01):119. |
| [11] | Li Y S;Chen Z .[J].Progress in Natural Science,2006,14(12):1099. |
| [12] | Zhang J;Chen Z .[J].Acta Physica Sinica,2009,58(01):631. |
| [13] | Chen L Q;Khachaturyan A G .[J].Scripta Metallurgica et Materialia,1991,25:61. |
| [14] | Wang Y;Khachaturyan A G .[J].Acta Metallurgica Et Materialia,1995,43:1837. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%