采用动电位极化测量技术测定了钛合金电极、石墨电极、不锈钢电极和铜电极在不同电解液浓度、不同温度和不同电流密度下的极化曲线。结果表明,在电解液为7%HCl（质量分数）与NaCl混合液,温度为70℃,电流密度为0.2A/cm2的条件下,以钛合金为阳极、不锈钢为阴极时过电位较小,槽电压较低,电压效率较高,能耗较小。
Using the dynamic potential polarization measurement technology,the polarization curves of titanium alloy,graphite,stainless steel and copper under the conditions of different electrolyte concentration,different temperatures and different current densities were measured.The results showed that when electrolyte was mixed with HCl（7%） and NaCl,electrolysis temperature was 70 ℃,current density was 0.2 A/cm2,the anodic material was titanium alloy and the cathodic material was stainless steel,the cell voltage was low,voltage efficiency was high and energy consumption was low.
参考文献
| [1] | 刘志新,吴丽君,郝章来.氯乙烯合成回收盐酸工艺技术的改进[J].中国氯碱,2004(07):21-23. |
| [2] | 张海东,张秀凤,孙金茂.废盐酸的再生利用[J].金属制品,2008(04):53-56. |
| [3] | 席英信,雍兴跃,郝彦军,吴斌.废盐酸回收新技术在冷轧厂的应用[J].轧钢,2009(02):25-27. |
| [4] | 张孟民,韩小龙,胡登伟,何柱生.工业酸洗含铁废盐酸的资源化处理工艺[J].环境保护科学,2007(05):21-23,57. |
| [5] | 王琴,孙根行,孙安妮.废盐酸电解回用技术研究[J].现代化工,2011(03):52-54. |
| [6] | 王莉,范洪波,李敬,郑伟,晁月盛,沈军.Fe_（41）Co_7Cr_（15）Mo_（14）C_（15）B_6Y_2块体非晶合金在HCl溶液中的腐蚀行为[J].稀有金属材料与工程,2009(11):1992-1996. |
| [7] | 姜应律,吴荫顺.利用极化曲线推测中性水溶液中钛合金表面的氧化还原反应机理[J].北京科技大学学报,2004(04):395-399. |
| [8] | 刘振江,张卫国.极化曲线在氯碱工业的应用[J].氯碱工业,2009(05):12-14,17. |
| [9] | 覃奇贤,刘淑兰.电极的极化和极化曲线（Ⅱ）--极化曲线[J].电镀与精饰,2008(07):29-34. |
| [10] | A.A. Jalali;F. Mohammadi;S.N. Ashrafizadeh .Effects of process conditions on cell voltage, current efficiency and voltage balance of a chlor-alkali membrane cell[J].Desalination: The International Journal on the Science and Technology of Desalting and Water Purification,2009(1/3):126-139. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%