用分析电镜和高分辨电镜确定了贝氏体钢中贝氏体铁素体和残余奥氏体之间存在3种取向关系.其中一种为K-S关系,即[(1)10]γ'//[1(1)1]α,(111)γ'//(110)α;一种为N-W取向关系,即[1(1)0]γ'//[001]α,(111)γ'//(110)α;还有一种为G-T关系,即[112]γ'//[110]α,(11(1))γ'//(1(1)0)α.高分辨像显示,贝氏体铁素体-奥氏体相界面不平直,α和γ '两相内有系列刃型位错和结构小台阶,两相界面未显示出连续的严格共格关系.
参考文献
| [1] | Nishiyama Z.Science Report[J].Tohoku lmp University,1934(23):325. |
| [2] | Smith G V;Mehl R F.Lattice Relationship in Decomposition of Austenite to Pearlitc,Bainite and Martensite[J].Transactions of the American Institute of Mining and Metallurgical Engineers,1942(150):211. |
| [3] | Pitsch W.Der Orientierungszusammenhang Zwischen Zementit und Austenit[J].Acta Metallurgica,1962(10):897. |
| [4] | 黄孝英.透射电子显微学[M].上海:上海科学技术出版社,1987 |
| [5] | Hoekstrs S.An Accurate and General Method of Determing Habit Planes and Orientation in Bainitic Steels and Verification of the IPS theory[A].TMS-AIME,1982:1017. |
| [6] | Srinivasan G R;Wayman C M.Transmission Electron Microscope Study of the Bainite Transformation in Iron Chromium-Carbon Alloys[J].Acta Metallurgica,1968(16):609. |
| [7] | 徐祖耀;刘世楷.贝氏体相变与贝氏体[M].北京:科学出版社,1991 |
| [8] | 方鸿生;王家军;杨志刚.贝氏体相变[M].北京:科学出版社,1999 |
| [9] | 刘宗昌;任慧平;王海燕.贝氏体与贝氏体相变[M].北京:冶金工业出版社,2009 |
| [10] | 孟凡妍 .高强韧贝氏体钢组织控制及精细结构[D].山东大学,2000. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%