采用核壳橡胶粒子CSR-1做环氧树脂的增韧剂,采用4,4'-二氨基二苯砜(DDS)做环氧树脂的固化剂制备了一种高温固化环氧基体树脂.实验结果表明,CSR-1的用量仅为5phr时基体树脂即获得了较好的增韧效果,冲击强度达到了29.1kJ/m2,比增韧前提高了近58％;断裂韧性GIC达到了306kJ/m2,比增韧前提高了93.7％;DMA和TG分析结果显示核壳橡胶粒子增韧基体树脂的的耐热性和模量几乎没有下降,玻璃化转变温度达到了190.4℃;通过基体树脂DSC放热曲线和流变特性确定了基体树脂的固化工艺条件为125℃×1h/185℃×4h,热熔法制备预浸料的成型温度为75～80℃.
参考文献
| [1] | 王琦杰;黄英;熊佳;李鹏.环氧树脂增韧研究进展[J].玻璃钢/复合材料,2004(5):50-54. |
| [2] | 冯浩,王德志,曲春艳,李洪峰.一种高温固化环氧基体树脂的研制[J].化学与黏合,2011(04):23-25. |
| [3] | 武渊博,李刚,黄智彬,李鹏.端环氧基丁腈橡胶增韧环氧树脂的结构与性能[J].玻璃钢/复合材料,2010(05):44-46,83. |
| [4] | 王安东,陈阳,李嘉生.改性环氧基复合材料工艺性能试验研究[J].玻璃钢/复合材料,2012(04):118-120. |
| [5] | H.J.Sue;J.L.Bertram;E.I.Garcia-Meitin;J.W.Wilchester,L.L.Walker.Fracture belavior of core-shell rubber-modified crosslinkable epoxy thermoplastic[J].Colloid and Polymer Science,1994(4):456-466. |
| [6] | Richard J.Day;Peter A.Lovell;Dorian Pierre.Toughening of Epoxy Resins using Particles Prepared by Emulsion Polymerization:Effects of Particle Surface Functionality,Size and Morphology on Impact Fracture Properties[J].Polymer International,1997(3):288-299. |
| [7] | Lu F.;Kausch HH.;Cantwell WJ. .THE ROLE OF CAVITATION AND DEBONDING IN THE TOUGHENING OF CORE-SHELL RUBBER MODIFIED EPOXY SYSTEMS[J].Journal of Materials Science,1997(11):3055-3059. |
| [8] | L.BECU-LONGUET;A.BONNET;C.PICHOT;H.SAUTEREAU,A.MAAZOUZ.Epoxy Networks Toughened by Core-Shell Particles:Influence of the Particle Structure and Size on the Rheological and Mechanical properties[J].Journal of Applied Polymer Science,1999(72):849-858. |
| [9] | Jiwon Choi;Albert F.Yee;Richard M.Laine .Toughening of Cubic Silsesquioxane Epoxy Nanocomposites Using Core-Shell Rubber Particles: A Three-Component Hybrid System[J].Macromolecules,2004(9):3267-3276. |
| [10] | KING-FU LIN;YOW-DER SHIEH.Core-Shell Particles Designed for Toughening the Epoxy Resins.Ⅱ.Core-Shell-Paaicle-Tough-ened Epoxy Resins[J].Journal of Applied Polymer Science,1998(70):2313-2322. |
| [11] | 何卫东,潘才元.核壳聚合物粒子[J].功能高分子学报,1997(01):110-117. |
| [12] | 范宏,王建黎.PBA／PMMA型核壳弹性粒子增韧环氧树脂研究[J].高分子材料科学与工程,2001(01):121-124. |
| [13] | 王巍 .丙烯酸酯核壳粒子的制备及增韧环氧树脂胶黏剂的研究[D].黑龙江省哈尔滨市:哈尔滨工程大学,2006. |
| [14] | 张凯,郝晓东,黄渝鸿,周德惠.用核壳型聚合物粒子增韧改性环氧树脂[J].化工新型材料,2003(12):14-17. |
| [15] | Weitao Wan;Demei Yu;Jian He;Yunchuan Xie Longbiao Huang Xiusheng Guo.Simultaneously Improved Tougheness and Dielectric Properties of Epoxy/Core-Shell Particle Blends[J].Journal of Applied Polymer Science,2008(107):1020-1028. |
| [16] | 杨涛,高殿斌,杨公源.宽幅预浸料用胶膜制备技术研究[J].玻璃钢/复合材料,2008(04):33-35. |
| [17] | 刘宝峰;李佩兰;张凤翻.热熔法预浸料制备工艺研究[J].高科技纤维与应用,2000(4):38-41. |
| [18] | 黑龙江省科学院石油化学研究院 .环氧基体树脂、预浸料及其制备方法和制备预浸料采用的装置[P].中国:ZL201010611628.7,2012-07-04. |
| [19] | 邱华,齐暑华,王劲.核壳聚合物增韧环氧树脂的研究及进展[J].中国胶粘剂,2006(06):37-41. |
| [20] | 舒卫国,杨熙,宋旻键."神舟七号"飞船舱外航天服防护头盔组件的研制[J].玻璃钢/复合材料,2010(01):57-59. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%