Interpenetrating polymer networks(IPNs)based on fluoroelastomer/butadiene-acrylonitrile rubber(FKM/NBR)by molten blending at a high temperature and chemical cross-linking of two components were prepared.The influence of the two networks component on the mechanical properties and thermostabilities was studied.The experimental results show that the mechanical properties of the IPNs are superior to those of the individual FKM and NBR networks due to forming the case of interpenetrating and intercross-linking between the two networks,the mechanical properties and thermal resistance exhibit higher values when 80/20(w/w)FKM and NBR is blended and respectively cured simultaneously.The co-continuous morphology of the IPNs in the blends of 80/20(w/w)FKM/NBR is found by transmission electron microscopy(TEM),the differential scanning calorimetry(DSC)determination shows that the blends of 80/20(w/w)FKM/NBR have better compatibility,and the glass transition temperature of the elastomer is -21.5℃.
参考文献
| [1] | C Louis;J F Chailan;P Bartolomeo et al.Supertoughness in Polysulfone/Poly(ethylene-octene) Blends[J].Polymer,2001,42:7107-7115. |
| [2] | N Chikhi;S Fellahi;M Bakar .Effect of Composition on the Fracture Toughness and Flexural Strength of Syntactic Foams[J].European Polymer Journal,2002,38:251-264. |
| [3] | Chen N P;Chen Y L;Wang D L et al.Interpenetrating Polymer Networks of Polyurethane and Vinglester Resin for Reactive Injection Molding Process[J].J Appl Ploy Sci,1992,46:2075-2080. |
| [4] | Mengjiao W;Huaiyao G;Guangzhi X.Handbook of Rubber Industry[M].北京:化学工业出版社,1989 |
| [5] | Frisch K C;Klempner D;Frisch H L .Recent Advance in Interpenetrating Polymer Networks[J].Polymer Engineering and Science,1982,22(17):1143-1152. |
| [6] | Corain B;Benedetto C .Interpenetrating Organometallic Polymer Network[J].Advanced Materials,1992,4(02):97-99. |
| [7] | Aji P. Mathew;S. Packirisamy;Sabu Thomas .Studies on the thermal stability of natural rubber/polystyrene interpenetrating polymer networks; thermogravimetric analysis[J].Polymer Degradation and Stability,2001(3):423-439. |
| [8] | Gupta N;Srivastava A K .Interpenetrating Polymer Networks from Poly(metal acrylates)[J].Synthesis and Properties Macromolecules,1995,28(04):827-831. |
| [9] | Tamai T;lmagawa A;Tran-Cong Q .Semi-interpenetrating Polymer Networks Prepared by in situ Photo-crosslinking of Miscible Polymer Blends[J].Macromolecules,1994,27(25):7486-7489. |
| [10] | Scott CE;Maeosko CW .Compounding and Morphology of Nylon/Ethylene-propylene Rubber Reactive and Non-reactive Blends[J].International Polym Proc,1995,36(01):231-233. |
| [11] | M. Abdul Kader;Anil K. Bhowmick .Thermal ageing, degradation and swelling of acrylate rubber, fluororubber and their blends containing polyfunctional acrylates[J].Polymer Degradation and Stability,2003(2):283-295. |
| [12] | A.P.Mathew;S.Packirisamy;H.J.Radusch;S.Thomas .Effect of initiating system, blend ratio and crosslink density on the mechanical properties and failure topography of nano-structured full-interpenetrating polymer netowrks from natural rubber and polystyrene[J].European Polymer Journal,2001(9):1921-1934. |
| [13] | Ali SAM;Hourston D .Thermoplastic Interpenetrating Polymer Networks Based on a Poly(styrene-b-butadiene)Copolymer and a Poly(styrene-co-sodium methacrylate)Ionomer[J].European Polymer Journal,1995,31(01):1-8. |
| [14] | M. S. El-Aasser;R. Hu;V. L. Dimonie;L. H. Sperling .Morphology, design and characterization of IPN-containing structured latex particles for damping applications[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,1999(1/3):241-253. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%