对平衡处理(300℃～340℃)后的Al-Zn及Al-Zn加Cu合金α1相成分进行了电子探针微区分析.确定了Cu对α1+α2溶解度间隙形状,即α1/(α1+α2)边界走向的影响.该边界随着Cu含量的增加,向低Zn侧偏移,而不是此前所确定的向高Zn侧偏移.这一结果支持近年的热力学计算结果,溶解度间隙呈"隧道形",而不支持根据实测相图推测的"钟罩形".
参考文献
| [1] | Koster W;Moeller K .[J].Zeitschrift fur Metallkunde,1941,33:284. |
| [2] | Tebharkt E .[J].Zeitschrift fur Metallkunde,1942,34:208. |
| [3] | Murphy S .[J].Metal Science Journal,1975,9:163. |
| [4] | Kuznetsov G M;Krivosheeva G B;Dolgova V E;Rassadina L A .Investigation of Alloys of the Al-Zn-Cu System[J].Tsvetnaya Metallurgiya,1986,14:61. |
| [5] | 郝士明,郝新江,李艳霞,任玉平,李洪晓,赵刚.Al-Zn-Cu系中的T'化合物与低Cu侧室温相关系[J].金属学报,2002(07):694-698. |
| [6] | Ren Y P;Ding H;Hao S M .[J].Journal of Materials Science Letters,2003,22:433-436. |
| [7] | Chen S L;Zhang F;Daniel S;Chang Y A,Aoates W,Schimid-Fetzer R.On the Calculation of Multicomponent Stable Phase Diagrams[A].Sendai:JIM,2000:57. |
| [8] | Murphy S .[J].Zeitschrift fur Metallkunde,1980,71:96. |
| [9] | Durman M;Murphy S .[J].Acta Metallurgica Et Materialia,1991,39(10):1024. |
| [10] | Murphy S .[J].Metal Science Journal,1975,9:163. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%