用连续退火模拟试验机,在实验室试制了冷轧高硅DP590,并通过扫描电镜、EBSD、透射电镜和力学性能测试研究了不同退火温度(735～835℃)对其组织和力学性能的影响.结果表明:退火温度对高硅双相钢强度和塑性有重要的影响,当退火温度为785℃时,材料获得良好的综合力学性能.不同温度退火后得到的组织均为铁素体和均匀分布在其晶界上的岛状马氏体；利用EBSD技术清晰地观察到离散分布于铁素体和马氏体晶界处的残余奥氏体.运用透射电镜观察到马氏体周围的位错线及位错团,这是双相钢连续屈服特性的重要保障.
参考文献
| [1] | 王辉,刘文艳,袁桂莲,林承江,韩荣东.不同实验条件对冷轧双相钢高温热塑性的影响及影响机制[J].钢铁研究学报,2008(12):35-39. |
| [2] | 唐荻,米振莉,陈雨来.国外新型汽车用钢的技术要求及研究开发现状[J].钢铁,2005(06):1-5. |
| [3] | 朱晓东,王利.连续退火工艺参数对Si-Mn系冷轧双相钢的力学性能的影响[C].2003中国钢铁年会论文集,2003:2571-2575. |
| [4] | Aydin Hüseyin,Kazdal Zeytin Havva,Kubilay Ceylan.Effect of Intercritical Annealing Parameters on Dual Phase Behavior of Commercial Low-Alloyed Steels[J].钢铁研究学报(英文版),2010(04):73-78. |
| [5] | 韩会全,霍刚,刘彦春,王国栋.连续退火过时效温度对热处理双相钢组织性能的影响[J].钢铁,2009(02):52-55. |
| [6] | Saleh M H;Priestner R .Retained Austenite in Dual-Phase Silicon Steels and Its Effect on Mechanical Properties[J].Journal of Materials Processing Technology,2001,113:587. |
| [7] | Nouri A;Saghafian H;Kheirandish Sh .Effect of Silicon Content and Intercritical Annealing on Manganese Partition in Dual Phase Steels[J].Journal of Iron and Steel Research International,2010,17(05):44. |
| [8] | 金光灿,赵爱民,赵征志,唐荻,刘利,周建.800MPa冷轧热镀锌双相钢组织性能及其织构演变[J].材料工程,2010(09):40-44. |
| [9] | Rocha RO;Melo TMF;Pereloma E;Santos DB .Microstructural evolution at the initial stages of continuous annealing of cold rolled dual-phase steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):296-304. |
| [10] | Yuki TOJI;Takako YAMASHITA;Katsumi NAKAJIMA .Effect of Mn Partitioning during Intercritical Annealing on Following γ->α Transformation and Resultant Mechanical Properties of Cold-rolled Dual Phase Steels[J].ISIJ International,2011(5):818-825. |
| [11] | 李麟.相变塑性钢--原理、性能、设计和应用[M].北京:科学出版社,2009 |
| [12] | 龙起易;曾大卫;谭古里 .双相钢中残余奥氏体对性能的影响及其热稳定化[J].金属热处理学报,1995,16(02):1. |
| [13] | Lee Y K;Shin H C;Jang Y C et al.Effect of Isothermal Transformation Temperature on Amount of Retained Austenite and Its Thermal Stability in a Bainitic Fe-3 ％ Si-0.45 ％ C-X Steel[J].Scripta Materialia,2007,47:805. |
| [14] | 邝霜,康永林,于浩,窦婷婷,尹显东,刘仁东.600MPa级冷轧双相钢的试制与研究[J].材料工程,2006(z1):329-333. |
| [15] | 马小亮;唐获;江海涛 等.DP800冷轧双相钢组织性能的研究[J].热加工工艺技术与材料研究,2008,9:53. |
| [16] | 马鸣图;吴宝榕.双相钢--物理和力学冶金[M].北京:冶金工业出版社,2009 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%