对薄板坯连铸连轧的低碳铝镇静钢中AlN的作用进行了初步的试验研究.研究结果显示:当低碳铝镇静钢中酸溶铝含量在0.005%～0.043%时,钢中AlN的沉淀析出对热轧板材的晶粒度及力学性能没有明显影响,据此可以推测AlN的沉淀析出不是薄板坯连铸连轧低碳铝镇静钢晶粒细化的原因.在薄板坯连铸连轧的低碳铝镇静钢中仅沉淀析出很少量的AlN,这些AlN仅能起到很微弱的沉淀强化作用,因此AlN也不是低碳铝镇静钢中起沉淀强化作用的主要析出相.但是这些少量AlN的沉淀析出对热轧板材再加热时的晶粒长大却有明显影响:随钢中酸溶铝含量的增加,即随钢中AlN含量的增加,钢的晶粒粗化温度不断提高.
参考文献
| [1] | Mohamed Sennour;Claude Esnouf .Contribution of advanced microscopy techniques to nano-precipitates characterization: case of AlN precipitation in low-carbon steel[J].Acta materialia,2003(4):943-957. |
| [2] | Michel J P;Jonas J J .Precipitation Kinetics and Solute Strengthening in High Temperature Austenite Containing Al and N[J].Acta Metallurgica,1981,29:513. |
| [3] | Erasmus L A;Mech E G I.Effect of Aluminum Additions on Forgeability,Austenite Grain Coarsening Temperature,and Impact Properties of Steel[J].Journal of the Iron and Steel Institute,1964(01):32. |
| [4] | Croft N H;Entwisle A R;Davies G J .Origins of Dendritic AlN Precipitates in Aluminum-Killed-Steel Castings[J].Metals and Technology,1983,10:125. |
| [5] | Gladman T;Pickering F B.Grain-Coarsening of Austenite[J].Journal of the Iron and Steel Institute,1967(06):653. |
| [6] | 陈襄武.炼钢过程的脱氧[M].北京:冶金工业出版社,1991:266. |
| [7] | 刘阳春 .薄板坯连铸连轧低碳铝镇静钢N、Al的作用与控制研究[D].北京:北京科技大学,2007. |
| [8] | 刘永铨.钢的热处理[M].北京:冶金工业出版社,1981:8. |
| [9] | 刘云旭.金属热处理原理[M].北京:机械工业出版社,1981:31. |
| [10] | 康永林;傅杰;柳得橹.薄板坯连铸连轧钢的组织性能控制[M].北京:冶金工业出版社,2006:376. |
| [11] | 雍歧龙;马鸣图;吴宝榕.微合金钢-物理和力学冶金[M].北京:机械工业出版社,1989:218. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%