为了进一步提高铝合金的耐腐蚀性能,利用两步法在6063铝合金表面制备Ce-Mn/Mo复合化学转化膜.采用扫描电镜、能谱仪、电化学测试对转化膜的组织结构和耐蚀性能进行表征.结果表明:Ce-Mn/Mo复合膜主要由Al,Mo,Ce,Mn的氧化物和氢氧化物组成,主要成膜元素Mo,Ce和Mn在膜层中分布规律基本一致;膜层组织致密且较厚,与基体间结合良好;Ce-Mn/Mo复合转化膜具有优异的电化学腐蚀性能,可显著降低6063铝合金的自腐蚀电流密度,使钝化区间变宽.
参考文献
| [1] | 盘艳红,杜军,李文芳,穆松林.AZ91镁合金表面Ce-Mn复合转化膜室温制备及其耐蚀性研究[J].表面技术,2011(03):40-43. |
| [2] | Choi JG.;Thompson LT. .XPS STUDY OF AS-PREPARED AND REDUCED MOLYBDENUM OXIDES[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,1996(2):143-149. |
| [3] | Gesheva KA;Ivanova T;Marsen B;Cole B;Miller EL;Hamelmann F .Structural and surface analysis of Mo-W oxide films prepared by atmospheric pressure chemical vapor deposition[J].Surface & Coatings Technology,2007(22/23):9378-9384. |
| [4] | Hughes A E .XPS and SEM characterization of hydrated cerium oxide conversion coating[J].Surface and Interface Analysis,1995,23(7/8):540-550. |
| [5] | Bach S.;Baffier N.;Pereiraramos JP. .A NEW MNO2 TUNNEL RELATED PHASE AS HOST LATTICE FOR LI INTERCALATION[J].Solid state ionics,1995(1/2):151-158. |
| [6] | Parida K M;Kanungo S B;Sant B R .Studies on MnO2-I.Chemical composition,microstructure and other characteristics of some synthetic MnO2 of various crystalline modifications[J].Electrochimica Acta,1981,26(03):435-443. |
| [7] | 张军军 .铝合金表面Ce-Mn转化膜常温制备及表征[D].广州:华南理工大学,2010. |
| [8] | 路长青.钼酸盐的缓蚀机理[J].材料保护,1996(10):22. |
| [9] | 王秋景,唐耀胜.弱碱性介质中钼酸盐系缓蚀剂的研制[J].电镀与精饰,2002(06):22-26. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%