采用快淬和晶化退火法制备了成分为Nd8.5Fe76.6-xGaxCo5Zr2.7B6.2(x=0～0.5)的纳米晶复合永磁粘结磁体,研究了其磁性能的变化.结果表明,适量Ga元素的添加能有效提高磁体退磁曲线的方形度,进而提高磁体的最大磁能积.Ga含量0.2%(原子分数),快淬速度为16.0m/s的合金经670℃/4min的晶化处理后,制得的粘结磁体具有较佳的磁性能:Br=0.745T,jHc=730.1kA/m,(BH)max=80.1kJ/m3.适量的Ga元素的添加可以提高磁体的温度稳定性.Ga含量为0.2%(原子分数)的合金具有较好的温度系数,在25～150℃温度区间内剩磁温度系数α=-0.091%/℃,内禀矫顽力温度系数β=-0.353%/℃.
参考文献
| [1] | Skomski R;Coey J M D .[J].Physical Review,1993,B48:15812. |
| [2] | Kneller E.F.;Hawig R. .The exchange-spring magnet: a new material principle for permanent magnets[J].IEEE Transactions on Magnetics,1991(4):3588-3560. |
| [3] | Akria A et al.[J].IEEE Transactions on Magnetics,2001,37(04):2555. |
| [4] | Chen Zhongmin;Hadjipanayis George C.;Chen Qun;Ma Baomin;Zhang Yong .Effect of wheel speed and subsequent annealing on the microstructure and magnetic properties of nanocomposite Pr2Fe14B/α-Fe magnets[J].Journal of Magnetism and Magnetic Materials,1999(1/2):8-16. |
| [5] | Angela D et al.[J].Journal of Magnetism and Magnetic Materials,2001,226-230:1428. |
| [6] | 王震;倪建森;徐晖.永磁材料结构和磁性能的研究[A].贵阳,2004:106. |
| [7] | 吴义生,倪建森,徐晖,王震,周邦新,黄照华.Nd10.1Fe（83.7-x-y）CoxZryB6.2永磁材料结构和磁性能的研究[J].中国稀土学报,2005(03):295-298. |
| [8] | Zhang X Y et al.[J].Journal of Physics:Condensed Mater,2001,13:3859. |
| [9] | Gao RW.;Liu HQ.;Feng WC.;Chen W.;Wang B.;Han GB.;Zhang P. .Influence of Co, Ga and Si on the microstructure and the magnetic properties for nanocomposite permanent alloys[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2002(2):187-190. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%