采用焊接热模拟技术模拟不同焊接热输入条件下,峰值温度为1350℃时对应近焊缝区的组织和性能,并对母材进行宏观力学特性测试；对比分析不同焊接热输入条件下所得近焊缝区的组织和性能.结果表明:经过3种不同焊接热输入所得近焊缝区的组织均由板条状贝氏体和少量碳化物组成；随着焊接热输入的增加,近焊缝区组织晶粒变大,贝氏体板条束变粗变厚,析出的碳化物数量增多,并且强度降低、韧性增强,但总体上跟母材的性能基本一致；当焊接线能量为12kJ/cm时近焊缝区达到最佳的强韧性匹配.
参考文献
| [1] | 陶鹏,张弛,杨志刚,Yoshio Terada,Naoki Doi,Masahiko Murata.高钢级管线钢的组织和力学性能[J].焊管,2008(02):19-22,26. |
| [2] | 孙宏.西气东输二线国产X80螺旋埋弧焊管性能分析[J].焊管,2010(02):13-16,20. |
| [3] | 周平;李辉.XI00、X120高强韧性管线钢的研发和应用综述[J].莱钢科技,2009(06):9-12. |
| [4] | Dhua S K;Mukerjee D;Sarma D S .Influence of thermomechanicl treatments on the microstructure and mechanical orpperties of HSLA-100 steel plates[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2003,34(02):241-253. |
| [5] | M. SHOME;O.N. MOHANTY .Continuous Cooling Transformation Diagrams Applicable to the Heat-Affected Zone of HSLA-80 and HSLA-100 Steels[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2006(7):2159-2169. |
| [6] | 张骁勇,高惠临,庄传晶,吉玲康.焊接热输入对X100管线钢粗晶区组织及性能的影响[J].焊接学报,2010(03):29-32. |
| [7] | S. Moeinifar;A. H. Kokabi;H. R. Madaah Hosseini .Role of tandem submerged arc welding thermal cycles on properties of the heat affected zone in X80 microalloyed pipe line steel[J].Journal of Materials Processing Technology,2011(3):368-375. |
| [8] | 张婷婷,陈小伟,文康,王旭,乔桂英,廖波.焊接热循环对X120管线钢组织和性能的影响[J].金属热处理,2008(06):95-98. |
| [9] | 徐学利,辛希贤,石凯,周勇.焊接热循环对X80管线钢粗晶区韧性和组织的影响[J].焊接学报,2005(08):69-72. |
| [10] | 张文钺.焊接冶金学:基本原理[M].北京:机械工业出版社,1999:162. |
| [11] | 张文钺.焊接冶金学:基本原理[M].北京:机械工业出版社,1999:168-172. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%