以SiO2为硅源,炭黑为碳源,Fe2 O3为催化剂,采用碳热还原法在氩气保护下制备SiC微粉,研究催化剂含量,合成温度对SiC生成、形貌的影响.实验结果表明:在原料中添加Fe2 O3粉,1350℃保温3h就能产生SiC微粉；由X射线衍射分析显示,在1450℃下保温3h基本上全部转化为晶粒尺寸在50 nm左右SiC微粉；在相同温度下,随着Fe2 O3用量的增加,SiC产率增加.添加Fe2O3能加快反应速度以及提高SiC微粉的生成量.
参考文献
| [1] | 张敏,王晓刚,陈进,邓丽荣,陆树河,华小虎.表面改性对β-SiC微粉流动性的影响[J].硅酸盐通报,2011(03):519-523. |
| [2] | 潘顺龙,杨岩峰,张敬杰,宋广智.水玻璃包覆炭黑直接制备超细SiC粉体[J].硅酸盐学报,2005(08):980-985. |
| [3] | 王福,曹文斌,孙加林,何荣亮.碳化硅微粉的低温合成与制备[J].材料导报,2008(02):126-128. |
| [4] | 张淑会,薛向欣,金在峰.铁矿石尾矿合成碳化硅粉末[J].硅酸盐学报,2006(05):596-600. |
| [5] | Sang Jin Kim;Seok-Min Yun;Young-Seak Lee .Characterization of nanocrystalline porous SiC powder by electrospinning and carbothermal reduction[J].Journal of industrial and engineering chemistry,2010(2):273-277. |
| [6] | Liu, ZC;Shen, WH;Bu, WB;Chen, HR;Hua, ZL;Zhang, LX;Li, L;Shi, JL;Tan, SH .Low-temperature formation of nanocrystalline beta-SiC with high surface area and mesoporosity via reaction of mesoporous carbon and silicon powder[J].Microporous and Mesoporous Materials,2005(1/2):137-145. |
| [7] | 李智敏,曹全喜,黄云霞,李桂芳,张文庆.溶胶-凝皎-碳热还原法制备富碳β-SiC纳米粉体[J].硅酸盐学报,2009(06):942-946. |
| [8] | 张利锋,燕青芝,沈卫平,葛昌纯.燃烧法合成高纯β-SiC超细粉的工艺参数[J].硅酸盐学报,2007(07):817-821. |
| [9] | 王东华;靳国强;郭向云 等.前躯体凝胶中催化剂含量对碳化硅结构和性能的影响[J].无机化学学报,2009,23(05):794-798. |
| [10] | Young-Jae Lee .Formation of Silicon carbide on carbon fibers by carbothermal reduction of silica[J].Diamond and Related Materials,2004(3):383-388. |
| [11] | Manabu Fukushima;Masayuki Nakata;You Zhou;Tatsuki Ohji;Yu-ichi Yoshizawa .Fabrication and properties of ultra highly porous silicon carbide by the gelation–freezing method[J].Journal of the European Ceramic Society,2010(14):2889-2896. |
| [12] | 丘泰,龚亦农,徐洁,李远强.碳热还原法低温合成SiC粉末的研究[J].江苏陶瓷,2001(02):12-15. |
| [13] | 林建新,郑勇,郑瑛,魏可镁.制备高比表面积碳化硅的几种影响因素[J].无机化学学报,2006(10):1778-1782. |
| [14] | A. Devecerski;M. Posarac;A. Egelja .Fabrication of SiC by carbothermal-reduction reactions of mountain leather asbestos[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2008(1/2):270-276. |
| [15] | 张淑会,薛向欣,杨合,刘欣.工艺因素对碳热还原法合成SiC的影响[J].材料导报,2005(z1):366-368,381. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%