采用改进的工艺路线制备了化学计量比的Pb(Zn1/3Nb2/3)O3-PbTiO3-BaTiO3陶瓷,二氧化钛和碳酸钡不经过预烧,与预反应粉体混合球磨,成型后直接烧结,在1100℃和1120℃分别保温1 h,2 h,4 h获得了100%钙钛矿结构的PZN-PT-BT陶瓷,最大密度7.418 g/cm3,最大介电常数7672.

Stoichiometric Pb(Zn1/3Nb2/3)O3-PbTiO3-BaTiO3(PZN-PT-BT) perovskite ceramics prepared by modified processing route were investigated. Without calcination of TiO2 and BaCO3, a mixture of pre-reaction powders (PbO+ZnNb2O6) and TiO2and BaCO3 was pressed and sintered directly. Stoichiometric PZN-PT-BT ceramics sintered at 1100℃ and 1120℃ for 1, 2 and 4 h, respectively, with 100% perovskite phase were obtained. PZN-PT-BT ceramics with density 7.418 g/cm3 (92.6% of theoretical density 8.01 g/cm3) and dielectric constant Kmax 7672 at 1 kHz were prepared. As far as energy-saving and time-saving of processing are concerned, it is a simplified and effective route to prepare PZN-PT-BT ceramics.

参考文献

[1] Service R E .[J].Science,1997,275:1878.
[2] Yamsshita Y;Harada K;Saitoh S .[J].FERROELECTRICS,1998,219:29.
[3] Cross L E .[J].Japanese Journal of Applied Physics,1995,34:2525.
[4] Kanagae T;Sakta K;Takenaka T .[J].JAPANESE JOURNAL OF APPLIED PHYSICS,1991,9B:2232.
[5] Shrout T R;Halliyal A .[J].AMERICAN CERAMIC SOCIETY OF BULLETIN,1987,64(04):704.
[6] Swartz S L;Shrout T R .[J].MaterRes Bull,1983,18:663.
[7] Lejeune M;Boilot J P .[J].Ceramics Int,1983,9(04):119.
[8] Guha J P .[J].Journal of Materials Science,1999,34:4985.
[9] Lucas P;Petuskey W T .[J].Journal of the American Ceramic Society,2001,84(09):2150.
[10] Swartz S L;Shrout T R .[J].Materials Research Bulletin,1982,17:1245.
[11] Halliyal A et al.[J].American Ceramic Society Bulletin,1987,66(04):671.
[12] Ravidranathan P;Komarneni S et al.[J].Journal of the American Ceramic Society,1991,74(12):2996.
[13] Fujin T;Tanaka A;Takenaka T .[J].JAPANESE JOURNAL OF APPLIED PHYSICS,1999,30:477.
[14] Wang J;Wan D etal .[J].JOURNAL OF THE AMERICAN CERAMIC SOCIETY,2001,82(02):2150.
[15] Xia F;Wang X;Yao X .[J].FERROELECTRICS,1998,215:181.
[16] Halliyal A;Safari A .[J].FERROELECTRICS,1994,158:295.
[17] Liou Y C;Tseng K H .[J].Materials Research Bulletin,2003,38:1351.
[18] Liou Y C .[J].Materials Letters,2004,58:944.
[19] Wang X;Chen H .[J].Journal of Applied Physics,2002,91(09):5979.
[20] Xia F.;Wang XL.;Yao X. .Effects of thermal annealing on the dielectric and piezoelectric properties of PZN-PT-BT ceramics[J].Journal of Materials Science Letters,1998(10):861-863.
[21] Wang X .[J].Journal of Materials Science,1999,34:6027.
[22] Pei Z;Che J et al.[J].Nature Science Edition,2003,4(01):77.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%