用现有的微弧氧化方法制备的镁合金陶瓷膜厚度有限,且属于多孔结构.采用电流密度0.4 A/dm2,在AZ61镁合金表面制备了陶瓷膜;研究了不同微弧氧化时间(30,50,70,90,120,160 min)对陶瓷膜微观性能的影响.结果表明:在电流密度一定的条件下,处理时间对陶瓷膜微观组织和性能有着较大的影响,随氧化时间延长,阳极电压、陶瓷膜厚度和粗糙度增大;孔隙率先增大后减小,最大值出现在70 min时,陶瓷膜表面熔融物颗粒和孔隙尺寸增大且分布不均;50 min时陶瓷膜耐蚀性最好.
参考文献
| [1] | 蒋百灵,张淑芬,吴国建,雷廷权.镁合金微弧氧化陶瓷层显微缺陷与相组成及其耐蚀性[J].中国有色金属学报,2002(03):454-457. |
| [2] | Yerokhin A L;Nie X;Leyland A et al.Plasma electrolysis for surface engineering[J].Surface and Coatings Technology,1999,122(2,3):75-91. |
| [3] | Krishna LR.;Somaraju KRC.;Sundararajan G. .The tribological performance of ultra-hard ceramic composite coatings obtained through microarc oxidation[J].Surface & Coatings Technology,2003(0):484-490. |
| [4] | Hani;Chol J H;Zhao B H.Micro-arc oxidation in various concentration of KOH and strcutural change by different cut off potential[J].Current Applied Physics,2007(07):23-27. |
| [5] | Fei Chen;Hai Zhou;Bin Yao;Zhen Qin;Qingfeng Zhang .Corrosion resistance property of the ceramic coating obtained through microarc oxidation on the AZ31 magnesium alloy surfaces[J].Surface & Coatings Technology,2007(9/11):4905-4908. |
| [6] | 杨晓飞,林文光,毛广雷.镁合金表面处理的现状及趋势[J].汽车工艺与材料,2007(03):10-13. |
| [7] | 梁浩成.金属腐蚀学导论[M].北京:机械工业出版社,1999:5-7. |
| [8] | 陈鸿海.金属腐蚀学[M].北京:北京理工大学出版社,1995:11-13. |
| [9] | 郭洪飞,安茂忠,霍慧彬,徐莘.工艺条件对镁合金微弧氧化的影响[J].材料科学与工艺,2006(06):616-621. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%