采用4种方法制备了VMgO催化剂样品(w(V2O5)=30%,w(MgO)=70%),并将其用于正丁烷氧化脱氢气固相反应.结果表明,MgO经蒸馏水回流和焙烧处理后再用NH4VO3溶液浸渍所制得的VMgO,对正丁烷氧化脱氢生成丁烯和丁二烯反应具有更好的催化性能.这是由于用该法制备的VMgO催化剂中存在较多的Mg3V2O8物种.通过添加Ni对VMgO催化剂进行了改性.结果表明,适量添加Ni(n(Ni)/n(V)=0.3)有利于催化剂中Mg3V2O8的生成,而Ni以Ni3V2O8的形态存在.由此明显改善了VMgO催化剂对正丁烷氧化脱氢生成丁烯和丁二烯反应的催化性能.
参考文献
| [1] | Grzybowska B;Sloczynski J;Grabowski R;Keromnes L,Wcislo K,Bobinska T.[J].Applied Catalysis A:General:279. |
| [2] | 照日格图,葛庆杰,李文钊,贾美林,于春英,徐恒泳.Ni-V-O催化剂上丙烷氧化脱氢制丙烯的反应[J].催化学报,2000(04):332-336. |
| [3] | 朱红娟,李洪波,佟建华,盛世善,杨维慎,林励吾.TiO2-ZrO2复合氧化物负载的氧化钒催化剂用于丙烷氧化脱氢反应[J].催化学报,2002(05):391-392. |
| [4] | Ortelli E E;Wambach J;Wokaun A.[J].Applied Catalysis A:General:227. |
| [5] | ChaarM A;Patel D;Kung M C;Kung H H.[J].Journal of Catalysis,1987(02):483. |
| [6] | Lemonidou A A;Tjatjopoulos G J;Vasalos I A .[J].Catalysis Today,1998,45(1-4):65. |
| [7] | Gao X T;Ruiz P;Xin Q;Guo X X, Delmon B.[J].Journal of Catalysis,1994(01):56. |
| [8] | KungHH;KungMC.[J].Applied Catalysis A:General:105. |
| [9] | Blasco T;Lopez Nieto J M.[J].Applied Catalysis A:General:117. |
| [10] | Corma A;Lopez Nieto J M;Paredes N.[J].Applied Catalysis A:General:161. |
| [11] | Lopez Nieto J M;Dejoz A;Vazquez M I;O'Leary W,Cunningham J .[J].Catalysis Today,1998,40(2/3):215. |
| [12] | 刘尧飞,王新平,田福平,贾翠英.正丁烷在金属钼酸盐催化剂上的氧化脱氢[J].催化学报,2004(09):721-726. |
| [13] | Sam D S H;Soenen V;Volta J C.[J].Journal of Catalysis,1990(02):417. |
| [14] | Dejoz A;Lopez Nieto J M;Marquez F;Vazquez M I.[J].Applied Catalysis A:General:83. |
| [15] | Lopez Nieto J M;Concepcion P;Dejoz A;Knozinger H,Melo F, Vazquez M I.[J].Journal of Catalysis,2000(01):147. |
| [16] | Solsona B;Dejoz A;Vazquez M I;Marquez F,Lopez Nieto J M.[J].Applied Catalysis A:General:99. |
| [17] | Chesnokov VV.;Bedilo AF.;Heroux DS.;Mishakov IV.;Klabunde KJ. .Oxidative dehydrogenation of butane over nanocrystalline MgO, Al2O3, and VOx/MgO catalysts in the presence of small amounts of iodine[J].Journal of Catalysis,2003(2):438-446. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%