以SiC陶瓷前驱体聚碳硅烷(polycarbosilane,PCS)为粘结剂、SiC微粉为填料、聚氨酯海绵为模板,低温制备出了SiC泡沫陶瓷.研究了SiC颗粒粒度和PCS含量对SiC泡沫陶瓷线收缩率、体积密度、微观结构与抗弯强度的影响.确定了不同粒度SiC颗粒制备泡沫陶瓷的最佳烧成温度.结果表明,随SiC颗粒粒度与PCS含量的增加泡沫陶瓷的线收缩率增大、体积密度降低；泡沫陶瓷的抗弯强度随SiC颗粒粒度的增大而降低；颗粒粒度小于1μm时,最佳烧成温度为1200℃,颗粒粒度大于1μm时,最佳烧成温度为1100℃；PCS在1100℃与1200℃热解可得到β-SiC晶粒,其晶粒尺寸为12.2 nm与19.6 nm.
参考文献
| [1] | Alvin M A;Lippert T E;Lane J E .Assessment of Porous Ceramic Materials for Hot Gas Filtration Applications[J].American Ceramic Society Bulletin,1991,70(09):1491-1498. |
| [2] | Young-Wook Kim;Shin-Han Kim;In-Hyuck Song .Fabrication of Open-Cell, Microcellular Silicon Carbide Ceramics by Carbothermal Reduction[J].Journal of the American Ceramic Society,2005(10):2949-2951. |
| [3] | X. BAO;M. R. NANGREJO;M. J. EDIRISINGHE .Preparation of silicon carbide foams using polymeric precursor solutions[J].Journal of Materials Science,2000(17):4365-4372. |
| [4] | X. Bao;M. R. Nangrejo .Synthesis of silicon carbide foams from polymeric precursors and their blends[J].Journal of Materials Science,1999(11):2495-2505. |
| [5] | 刘岩,姚秀敏,黄政仁,董绍明,江东亮.金属过滤器用高性能碳化硅泡沫陶瓷的制备[J].硅酸盐学报,2004(02):107-112. |
| [6] | 姚秀敏,谭寿洪,黄政仁.聚氨酯海绵的预处理对网眼多孔陶瓷性能的影响[J].硅酸盐学报,2005(10):1215-1219. |
| [7] | 姚秀敏,黄政仁,谭寿洪.聚碳硅烷低温烧结碳化硅网眼多孔陶瓷的研制[J].无机材料学报,2010(02):168-172. |
| [8] | 杜庆洋.有机前驱体浸渍法制备碳化硅泡沫陶瓷的性能改进[J].硅酸盐通报,2007(03):580-582,597. |
| [9] | 苏鹏,郭学益,冀树军.SiC泡沫陶瓷的凝胶注模制备与表征[J].人工晶体学报,2009(04):983-988. |
| [10] | 熊亮萍,许云书.陶瓷先驱体聚合物的应用[J].化学进展,2007(04):567-574. |
| [11] | 邰金华,余煜玺,赖德林,许春来.陶瓷先驱体Polyvinylsilazane-b-Polystyrene的合成及纳米陶瓷颗粒的制备[J].人工晶体学报,2011(05):1266-1270. |
| [12] | 孙东飞,于升学,谢丹阳,阎兴斌,谢征芳,薛群基.静电纺丝法制备SiC纤维及其表征[J].人工晶体学报,2010(06):1559-1563. |
| [13] | 刘卫,黎阳,陈璐.聚碳硅烷低温制备碳化硅泡沫陶瓷[J].硅酸盐学报,2011(11):1763-1767. |
| [14] | Ly H Q;Taylor R;Day R J.Conversion of Polycarbosilane (PCS) to SiC-based Ceramic Part Ⅱ Pyrolysis and Characterisation[J].Journal of Materials Science,2000:4045-4057. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%