研究微量元素的种类与添加量对Cu55Zr38Al7铜基块体金属玻璃形成能力的影响.X射线衍射仪和差示扫描量热仪的研究表明,添加2at%的Ag、Ti、Y或Nd都可以提高Cu55Zr38Al7的玻璃形成能力;6at%的Ag替代Cu,金属玻璃棒的临界直径可从2 mm增加到4 mm;而复合添加2at%的Ag和Y也可以明显提高Cu55Zr38Al7的玻璃形成能力.所以,替代化学性质相似的元素或者扩大合金系的原子尺寸范围可显著提高铜基块体金属玻璃的形成能力.
参考文献
[1] | Chen QJ;Fan HB;Ye L;Ringer S;Sun JF;Shen J;McCartney DG .Enhanced glass forming ability of Fe-Co-Zr-Mo-W-B alloys with Ni addition[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):188-192. |
[2] | Ma D;Cao H;Ding L et al.[J].Applied Physics Letters,2005,87(17):171914. |
[3] | Liang W Z;Shen J;Sun J F .[J].Journal of Alloys and Compounds,2006,420(1-2):94. |
[4] | Zhang T;Yamamoto T;Inoue A .[J].Materials Transactions-Japan Institute of Metals,2002,43(12):3222. |
[5] | N. Mitrovic;S. Roth;J. Eckert .Kinetics of the glass-transition and crystallization process of Fe_(72-x)Nb_(x)Al_(5)Ga_(2)P_(11)C_(6)B_(4) (x=0,2) metallic glasses[J].Applied physics letters,2001(15):2145-2147. |
[6] | Xiulin Ji;Ye Pan .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2008,485(1-2):154. |
[7] | Dwight E Gray.American Institute of Physics Handbook[M].New York:McGraw-Hill,1972 |
[8] | Fu HM;Wang H;Zhang HF;Hu ZQ .The effect of Gd addition on the glass-forming ability of Cu-Zr-Al alloy[J].Scripta materialia,2006(2):147-150. |
[9] | Dai C L;Guo H;Shen Y et al.[J].Scripta Materialia,2006,54(07):1403. |
[10] | Zhang Q S;Zhang W;Inoue A .[J].Scripta Materialia,2006,55(08):711. |
[11] | Men H;Zhang T .[J].Materials Transactions-Japan Institute of Metals,2005,46(07):1692. |
[12] | Xu D H;Duan G;Johnson W L .[J].Physical Review Letters,2004,92(24):245504. |
[13] | Ran Li;Shujie Pang;Chaoli Ma;Tao Zhang .Influence of similar atom substitution on glass formation in (La–Ce)–Al–Co bulk metallic glasses[J].Acta materialia,2007(11):3719-3726. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%