在实验室条件下,对一种微合金高强度钢进行热膨胀试验和热轧试验,测定了该试验钢的连续冷却转变动力学(CCT)曲线,并研究了不同温度转变的组织和第二相的体积分数、尺寸对其力学性能的影响.试验结果表明:变形温度的降低,贝氏体转变开始温度与转变结束温度均升高,硬度值也出现不同程度的提高;变形温度的降低,使得不同冷却速度下组织细化程度存在明显差异.利用合理控轧控冷工艺,使得屈服强度均达到690MPa以上,-30℃冲击功均达到230J以上.其中,第二相粒子在整个基体内呈细小弥散分布,起到有效的强化作用并改善钢的冲击韧性.
参考文献
| [1] | Rodrigues P C M;PerelomaE V;SantocDB .Mechanical Properities of an HSLA Bainitac Steel Subjected to Controlled Rolling With Accelerated Rolling[J].Materials Science and Engineering,2000,A 283:136. |
| [2] | Shuji Okaguchi.Production and Development of Linepipe Steel in Grade X100 and X120[A].北京,2005 |
| [3] | Kooj Y;Luton M J;Bangaru N V.Metallurgical Design of Ultrahigh Strength Steels for Gas Pipelines[A].Honolulu,USA,2003 |
| [4] | L.Barsanti;R.Bruschi;E.Donati.From X80 to X100:KnowHow Reached by ENI Group on High Strength Steel[A].Yokohama,Japan,2002 |
| [5] | Endo S;Ishikawa N;Kodo J.Advance in High Performance Linepipe With Respect to Strength and Deformability[A].Yokohama,Japan,2002 |
| [6] | Chiaki OUCHI .Development of Steel Plates by Intensive Use of TMCP and Direct Quenching Processes[J].ISIJ International,2001(6):542-553. |
| [7] | GBT 1172-1999.黑色金属硬度及强度换算值[S].北京:中国标准出版社,1999. |
| [8] | 衣海龙,杜林秀,王国栋,刘相华.X80管线钢的组织与性能研究[J].东北大学学报（自然科学版）,2008(02):213-216. |
| [9] | Crave A.J.;He K. .COMPLEX HETEROGENEOUS PRECIPITATION IN TITANIUM-NIOBIUM MICROALLOYED Al-KILLED HSLA STEELS-I. (Ti,Nb)(C,N) PARTICLES[J].Acta materialia,2000(15):3857-3868. |
| [10] | 翁宇庆.超细晶钢-钢的组织细化理论与控制技术[M].北京:冶金工业出版社,2003 |
| [11] | 马立强 .Nb、Ti钢宽厚板控制轧制中的再结晶和析出规律[D].东北大学,2007. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%