以Al-Cr2 O3为主反应体系,采用自反应淬熄法,研究了120 mm、170 mm、220 mm、400 mm不同淬熄距离对制备空心陶瓷微珠的影响.采用SEM、XRD、EDS、水淬熄等方法对淬熄产物表征与分析.实验结果表明:120mm距离下喷射,淬熄产物较原始团聚粉变化不大；170 mm下喷射,团聚粉粒径相对减小并有熔融现象,出现球形颗粒；220 mm下喷射,规则球形颗粒明显增加但仍有一部分不规则状团聚颗粒,400 mm下喷射,淬熄产物基本由球形或类球形颗粒组成,粒径分布较均匀且内部为空心结构.不同淬熄距离下完成自蔓延反应的程度与反应产生的气体是影响空心复相陶瓷微珠形成的根本原因.
参考文献
| [1] | 邓秀文.吸波材料研究进展[J].化工时刊,2007(08):58-65. |
| [2] | 蔡楚江,俞晓正,沈志刚,麻树林,邢玉山.空心微珠表面金属化研究[J].现代化工,2006(z1):241-244. |
| [3] | Geleil AS;Hall MM;Shelby JE .Hollow glass microspheres for use in radiation shielding[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2006(6/7):620-625. |
| [4] | Schmitt ML;Shelby JE;Hall MM .Preparation of hollow glass microspheres from sol-gel derived glass for application in hydrogen gas storage[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2006(6/7):626-631. |
| [5] | 王建江;温晋华;胡文斌.于Ti-B4C-C反应体系制备空心陶瓷沉珠的方法与机理研究[J].功能材料 |
| [6] | 娄鸿飞,王建江,胡文赋,程勇.基于Al-SiO2-蔗糖体系制备空心陶瓷微珠[J].复合材料学报,2011(02):174-178. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%