采用有限元法计算模拟了Al2 O3/MgAl2 O4共晶陶瓷区域熔炼定向凝固过程固液界面形貌的演变,研究了熔区坩埚壁面温度、凝固速率对固液界面形貌的影响.结果表明,当熔区坩埚壁面温度从2090℃升至2290℃时,固液界面先由凸界面转为平界面,再转变为凹界面;固液界面前沿的温度梯度随之增大.当凝固速率从1×10-6 m/s升至1 x10-5s时,固液界面形貌无明显变化,而熔区长度有所增大.随着凝固过程的进行,熔区长度逐渐增大,凸固液界面的凸出高度逐渐变小.

参考文献

[1] Sun H J S;Zhang J;Deng Y F et al.A Modified Preparation Technique and Characterization of Directionally Solidified Al2 O3/Y3 A15 O12 Eutectic in situ Composites[J].Scripta Materialia,2009,60:362-365.
[2] Waku Y. .A new ceramic eutectic composite with high strength at 1873 K[J].Advanced Materials,1998(8):615-617.
[3] Mizutani Y.;Yasuda H.;Ohnaka I.;Maeda N.;Waku Y. .Coupled growth of unidirectionally solidified Al2O3-YAG eutectic ceramics[J].Journal of Crystal Growth,2002(3/4):384-392.
[4] A.SAYIR;S.C. FARMER .THE EFFECT OF THE MICROSTRUCTURE ON MECHANICAL PROPERTIES OF DIRECTIONALLY SOLIDIFIED Al_2O_3/ZrO_2(Y_2O_3) EUTECTIC[J].Acta materialia,2000(18/19):4691-4697.
[5] Fritsch M;Klemn H .The Water Vapor Hot Has Corrosion of MGC Materials with Al2 O3 as a Phase Constituent in a Combustion Atmosphere[J].Journal of the European Ceramic Society,2008,28:2353-2358.
[6] 潘传增;赵忠民;张龙 等.添加剂对超重力下燃烧合成Al2O3/ZrO2 (4Y)的影响[J].人工晶体学报,2009,38(z1):350-354.
[7] J.H.Lee;A.Yoshikawa;H.Kaiden .Microstructure of Y_2O_3 doped Al_2O_3/ZrO_2 eutectic fibers grown by the micro-pulling down method[J].Journal of Crystal Growth,2001(1/2):179-185.
[8] Javier LLorca;Victor M. Orera .Directionally solidified eutectic ceramic oxides[J].Progress in materials science,2006(6):711-809.
[9] 常国威;王建中.金属凝固过程中的晶体生长与控制[M].北京:冶金工业出版社,2002
[10] 刘俊成,王友林,郭喜平.强化换热对CdZnTe晶体生长过程的影响[J].材料科学与工艺,2004(05):460-466.
[11] 许广济,丁雨田,阎威武,杜红林,赵谨红.热型连铸工艺凝固过程的数值模拟[J].甘肃工业大学学报,1999(02):17-21.
[12] 王维,倪锋.热型连铸过程的二维稳态传热模型[J].郑州大学学报(工学版),2005(04):62-65.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%