采用共沉淀法制备了Fe基预合金粉,并进行了不同温度下的烧结实验,对烧结后的试样块进行了力学性能测试及结构表征.结果表明,在共沉淀过程中该预合金粉已经形成了固溶体,实现了合金化,粉末的微观结构更有利于烧结的进行.预合金粉的烧结温度不宜超过900℃,最佳烧结温度为850℃,在此温度下试样具有较好的综合力学性能.烧结体的SEM观察表明在850℃烧结温度下材料的微观结构比较均匀,无明显晶粒长大,胎体材料对金刚石的包镶能力也最好.
参考文献
| [1] | LI Wensheng,ZHANG Jie,WANG Shucai,DONG Hongfeng,LI Yaming,LIU Yi.Characterizations and mechanical properties of impregnated diamond segment using Cu-Fe-Co metal matrix[J].稀有金属（英文版）,2012(01):81-87. |
| [2] | Structure, microstructure and mechanical properties of PM Fe-Cu-Co alloys[J].Materials & design,2010(1):522-526. |
| [3] | S. Spriano;Q. Chen;L. Settineri;S. Bugliosi .Low content and free cobalt matrixes for diamond tools[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2005(2):1190-1196. |
| [4] | 罗锡裕,麻洪秋,黄漫,唐明强.金刚石工具预合金代钴粉末的研究及应用[J].金刚石与磨料磨具工程,2006(01):18-24. |
| [5] | 黄艳华,贺跃辉,谢志刚,向波.金刚石工具用Ni-Co合金粉末的制备及表征[J].超硬材料工程,2006(05):1-5. |
| [6] | Hsieh YZ.;Lin ST. .Diamond tool bits with iron alloys as the binding matrices[J].Materials Chemistry and Physics,2001(2):121-125. |
| [7] | 韩娟,姚炯彬,葛启录,刘一波.碳含量对高铁基胎体金刚石工具性能的影响[J].粉末冶金材料科学与工程,2011(04):625-629. |
| [8] | 申思,宋月清,汪礼敏,张景怀.浅析共沉淀法制备Fe-Co预合金粉末中氧含量的控制[J].粉末冶金工业,2009(06):1-4. |
| [9] | 淦作腾,任淑彬,沈晓宇,何新波,曲选辉,郭佳.放电等离子烧结法制备金刚石/Cu复合材料[J].粉末冶金材料科学与工程,2010(01):59-63. |
| [10] | 戴秋莲,徐西鹏,王永初.金属结合剂对金刚石把持力的增强措施及增强机制评述[J].材料科学与工程,2002(03):465-468. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%