在分析相变温度和显微组织的基础上,采用低频扭摆仪研究了镍-镓-铁系铁磁性形状记忆合金的阻尼性能与应变振幅、频率及温度的关系.结果表明:Ni52Ga27Fe21合金的马氏体相变为热弹性马氏体相变,特征温度Ms、Mf、As、Af分别为69.3℃,60.2℃,93.6℃,102.6℃,室温下组织为板条状马氏体;镍-镓-铁系合金室温时的阻尼性能主要依赖于频率,Ni52Ga27Fe21合金的阻尼类型为阻尼共振型,而Ni53Ga27Fe20和Ni50Ga27Fe23合金的为滞弹性阻尼型;Ni52Ga27Fe21合金在马氏体相和奥氏体相共存时具有高阻尼性能,最大阻尼值为0.016.
参考文献
| [1] | Manfred Wuttig;Jian Li;Corneliu Craciunescu .A NEW FERROMAGNETIC SHAPE MEMORY ALLOY SYSTEM[J].Scripta materialia,2001(10):2393-2397. |
| [2] | N. Dealing;A. G. Jenner .Magnetic and Magnetoelastic Properties of Melt-Spun Ni-Mn-Ga[J].IEEE Transactions on Magnetics,2006(1):78-80. |
| [3] | V. A. Chernenko;J. Pons;E. Cesari;I. K. Zasimchuk .Transformation behaviour and martensite stabilization in the ferromagnetic Co-Ni-Ga Heusler alloy[J].Scripta materialia,2004(2):225-229. |
| [4] | A. Fujita;K. Fukamichi;F. Gejima .Magnetic properties and large magnetic-field-induced strains in off-stoichiometric Ni-Mn-Al Heusler alloys[J].Applied physics letters,2000(19):3054-3056. |
| [5] | 夏明六,马立群,阮爱杰,张平,丁毅.铁磁性形状记忆合金Ni50Ga27Fe17Co6的阻尼性能[J].机械工程材料,2009(03):50-52,100. |
| [6] | 郑红星,刘剑,夏明许,李建国.Ni-Fe-Ga磁致形状记忆合金中间马氏体相变[J].物理学报,2005(04):1719-1721. |
| [7] | 徐祖耀.相变内耗与伪滞弹性[J].金属学报,2003(11):1121-1126. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%