报告了作者利用机械球磨方法成功制备纳米晶NiZn铁氧体软磁材料的实验结果.实验样品具有很好的单相结构,所形成材料典型晶粒尺度为10～50nm.结合纯Fe3O4球磨样品,初步估算其样品的合成效率大约为27%～44%,这一结果可利用两步合成及中间纳米颗粒的高活性给予理解.对本实验利用球磨方法直接获得的NiZn铁氧体样品表现出较低的磁化强度σm和较大的矫顽力Hc,其典型值为43Am2kg-1和377×103(4π)-1A/m.从实用化角度而言,必要的热处理将是必要的.实验进一步证明,除了传统的机械合金化制备纳米晶软磁合金材料以外,利用高能球磨制备纳米晶NiZn软磁铁氧体也将是一种有效可行的新方法.
参考文献
| [1] | Bowen C R;Derby B .[J].British Ceramic Transactions,1997,96(01):25-26. |
| [2] | Yue Z;Zhou J;Li L et al.[J].Journal of Magnetism and Magnetic Materials,2001,233:224-229. |
| [3] | Kim JS.;Ahn JR. .Characterization of wet processed (Ni, Zn)-ferrites for CO2 decomposition[J].Journal of Materials Science,2001(19):4813-4816. |
| [4] | Kim W C;Kim S J;Lee S W et al.[J].Journal of Magnetism and Magnetic Materials,2001,226-230:1418-1420. |
| [5] | Verma A;Goel T C;Mendiratta R G et al.[J].Journal of Magnetism and Magnetic Materials,2000,208:13-19. |
| [6] | Jiang J S;Gao L;Yang X L et al.[J].Journal of Materials Science Letters,1999,18:1781-1783. |
| [7] | Rochman N T;Kawamoto K;Sueyoshi H et al.[J].Journal of Materials Processing Technology,1999,89-90:367-372. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%