The aging properties of Cu-0.35Cr-0.038Zr-0.055Ce alloy are studied. The results show that can obtain higher electrical conductivity and microhardness after solutioned at 920℃for lh, and aged at 500℃. The process of precipitation of the secondary phase can be accelerated with cold deformation before aging, so properties of the alloy are improved.Upon aging at 500℃ for 30 minutes after 60% cold deformation, the values of electrical conductivity and microhardness are69.0%IACS and 152HV respectively, but they are only 66.2%IACS and 136HV upon directly aging after solution. With the addition of a trace of rare earth element Ce, the value of microhardness of Cu-0.35Cr-0.038Zr alloy increases 18～25HV,while the value of electrical conductivity drops a little.
参考文献
| [1] | Kang BX;Cao XG;Huang JL;Yen B;Gu HC;Liu P .Aging precipitation and recrystallization of rapidly solidified Cu-Cr-Zr-Mg alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(1/2):262-267. |
| [2] | Batra IS.;Kulkarni UD.;Banerjee S.;Dey GK. .Microstructure and properties of a Cu-Cr-Zr alloy[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2001(2):91-100. |
| [3] | Tu J P;Qi W X .Effect of aging treatment on the electrical sliding wear behavior of Cu-Cr-Zr alloy[J].Wear,2002,249:1021-1027. |
| [4] | Liu P;Cao X G .Factors account for electrical conductivity of rapidly solidified Cu-Cr alloy[J].Journal of Luoyang Institution of Technology,1998,19:1-5. |
| [5] | Dong Z L;Tang X Y .Aging precipitation of Cu-Cr and Cu-Zr-Si alloys and affected by cold working[J].金属学报,1989,25(06):462-465. |
| [6] | 谢春生,周健,任合,周海良.稀土铬锆铜合金强化工艺研究[J].金属热处理,2001(06):12-14. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%