为获取高性能药型罩材料，采用铜模水淬制备W-Cu-Zr六元非晶合金。该非晶合金以Cu-Zr-Ni系铜基非晶为母合金，添加钨、钽、硼、锆、镍等元素，并根据各元素原子半径、密度、熔点、沸点，确定出最佳配比组合。结果表明：采用此材料制得?10 mm×50 mm圆柱形试样的抗拉强度为1820 MPa，伸长率为16.5%，断裂强度达2030 MPa，综合性能优越，用于药型罩材料有利于提高侵彻威力。
In order to obtain high performance liner material,W-Cu-Zr amorphous alloys with six elements were prepared by copper-formed mold water quenching method. W-Cu-Zr amorphous alloy was based on Cu-Zr-Ni amorphous alloy,adding tungsten,tantalum,boron,zirconium,nickel and other elements. The best combination ratio was determined on the atomic radius of each element,density,melting point,boiling point. Cylindrical specimen ?10 mm×50 mm was made of the obtained material,the tensile strength,elongation and the fracture strength is 1 820 MPa,16.5%and 2 030 MPa,respectively. The liner with this material can improve the penetration ability,due to its superior comprehensive performance.
参考文献
| [1] | 王毅,姜炜,刘宏英,李凤生.聚能装药粉末药型罩材料技术的发展和现状[J].爆破器材,2007(05):33-36. |
| [2] | 赵燕春 .Cu基块体金属玻璃的组织、热稳定性和力学性能研究[D].兰州理工大学,2010. |
| [3] | 董帮少,李德仁,陆曹卫,卢志超,周少雄.一种预测非晶合金的非晶形成能力新判据[J].金属功能材料,2011(03):70-73. |
| [4] | 彭谦之,刘克明,周海涛,赵博,周啸,刘瑞蕊.铜基非晶合金的研究现状及展望[J].热处理技术与装备,2012(05):1-4,7. |
| [5] | 陈春玲.原子尺寸因素对块体非晶形成能力的影响[J].河南理工大学学报：自然科学版,2011(04):472-476. |
| [6] | 王清,羌建兵,王英敏,夏俊海,林哲,张新房,董闯.Cu-Zr-Ti系Cu基块体非晶合金的形成和成分优化[J].物理学报,2006(01):378-385. |
| [7] | 王仁军 .铜基非晶复合材料的制备与力学性能研究[D].兰州理工大学,2010. |
| [8] | 冯柳 .铜基块状非晶合金的制备及其性能测试研究[D].兰州理工大学,2004. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%