通过利用光发射谱技术,探测了大功率直流喷射电弧等离子体增强化学气相沉积方法中沉积区域的气相激元分布,进而优选了金刚石生长的位置.在沉积过程中,不断使衬底做背向等离子体的运动,实现了大颗粒金刚石的连续生长,颗粒尺寸达到约1 mm3.采用劳厄背反射X射线衍射测试技术和拉曼谱技术,对所制备的样品进行了测试,结果表明:所制备的颗粒为金刚石单晶.对于大尺寸衬底,研究了背向运动速度对沉积晶体的形貌和质量的影响,发现了ATG型不稳定形貌.
参考文献
| [1] | 顾长志.晶粒尺寸和取向对金刚石膜热导率的影响[J].人工晶体学报,1997(03):327. |
| [2] | Mainwood A .CVD Diamond Pariicle Detectors[J].Diamond and Related Materials,1998,7:504-509. |
| [3] | Liao MY;Koide Y;Alvarez J;Imura M;Kleider JP .Persistent positive and transient absolute negative photoconductivity observed in diamond photodetectors[J].Physical review, B. Condensed matter and materials physics,2008(4):045112-1-045112-9-0. |
| [4] | T. Watanabe;T. Teraji;T. Ito .Fabrication of diamond p-i-p-i-p structures and their electrical and electroluminescence properties under high electric fields[J].Diamond and Related Materials,2007(1):112-117. |
| [5] | Gicquel A;Hassouni K;Silva F et al.CVD Diamond Films:from Growth to Applications[J].Current Applied Physics,2001,1:479-496. |
| [6] | Takatoshi Yamada;Hiromichi Yoshikawa;Hiroshi Uetsuka .Cycle of two-step etching process using ICP for diamond MEMS applications[J].Diamond and Related Materials,2007(4/7):996-999. |
| [7] | Yan C S;Vohra Y K;Mao H K et al.Very High Growth Rate Chemical Vapor Depesition of Single-crystal Diamond[J].Proceedings of the National Academy of Sciences(USA),2002,99(20):12523-12525. |
| [8] | Mao WL.;Mao HK.;Eng PJ.;Trainor TP.;Newville M.;Kao CC.;Heinz DL. Shu JF.;Meng Y.;Hemley RJ. .Bonding changes in compressed superhard graphite[J].Science,2003(5644):425-427. |
| [9] | Y. Mokuno;A. Chayahara;H. Yamada .Improving purity and size of single-crystal diamond plates produced by high-rate CVD growth and lift-off process using ion implantation[J].Diamond and Related Materials,2009(10):1258-1261. |
| [10] | Y. Mokuno;A. Chayahara;Y. Soda .Synthesizing single-crystal diamond by repetition of high rate homoepitaxial growth by microwave plasma CVD[J].Diamond and Related Materials,2005(11/12):1743-1746. |
| [11] | Q. Zhang;H.D. Li;S.H. Cheng .The effect of CO_2 on the high-rate homoepitaxial growth of CVD single crystal diamonds[J].Diamond and Related Materials,2011(4):496-500. |
| [12] | Qi Liang;Chih-shiue Yan;Yufei Meng .Recent advances in high-growth rate single-crystal CVD diamond[J].Diamond and Related Materials,2009(5/8):698-703. |
| [13] | Kuo CT.;Lin CH.;Lu TR.;Sung CM.;Wu JY. .Internal stresses and microstructures of commercial thick diamond films deposited by different deposition methods[J].Materials Chemistry and Physics,2001(2):114-120. |
| [14] | A.R. Davies;J.E. Field;K. Takahashi .Tensile and fatigue strength of free-standing CVD diamond[J].Diamond and Related Materials,2005(1):6-10. |
| [15] | F.X. Lu;W.Z. Tang;T.B. Huang .Large area high quality diamond film deposition by high power DC arc plasma jet operating at gas recycling mode[J].Diamond and Related Materials,2001(9-10):1551-1558. |
| [16] | Ohtake N;Yoshikawa M .Diamond Film Preparation by Arc Discharge Plasma Jet Chemical Vapor Deposition in the Methane Atmosphere[J].Journal of the Electrochemical Society,1990,137:717-722. |
| [17] | Grant Lu;Gray K J;Borchelt E F et al.Free-standing White Diamond for Thermal and Optical Applications[J].Diamond and Related Materials,1993,2:1064-1068. |
| [18] | Grinfeld M A .The Stress Driven Instability in Elastic Crystals:Mathematical Models and Physical Manifestations[J].Journal of Nonlinear Science,1993,3:35-83. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%