探索了通过加入金属Mn并结合熔体热处理工艺来控制铝硅合金中富铁相的形态.结果表明:熔体经过预先热处理后,加入Mn可以使绝大多数针状铁相转变成块状铁相,且粒径均一;预先热处理可以减少Mn的加入量而取得较好的效果,适宜的加入量为x(Mn)/x(Fe)=0.5~1.1(摩尔比),并可以通过控制Mn的加入量来控制块状富铁相杂质的粒径大小;经过联合处理的含铁铝硅合金的抗拉强度提高40~80 MPa,伸长率提高6%~7%.

参考文献

[1] 印飞,杨江波,孙宝德.铝硅合金中的六角形铁相[J].上海交通大学学报,2001(03):477-480.
[2] Narayanan L A;Samuel F H;Gruzleski J E .Crystallization behavior of iron-containing inter-metallic compound in 319 aluminum alloy[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1992,25A:1761.
[3] Sigworth G K;Shivkuman S;Apelian D .The influence of mohen metal processing on mechanical properties of cast Al-Si-Mg alloy[J].AFS Transactions,1989,139:811-824.
[4] Awano Y;Shimizu Y .Non-equilibrium crystallization of AlSiFe compound in melt-superheated Al-Si alloy casting[J].AFS Transactions,1990,176:889-896.
[5] Couture A .Iron in aluminum casting alloys-A literature survey[J].AFS Transactions,1981,11:9-17.
[6] Muali S;Raman K S;Murthy K S S .Morphological studies on β-FeSiAl5 phase in Al-7Si-0.3Mg alloy with trace addition of Be, Mn, Cr and Co[J].Materials Characterization,1994,33:99-112.
[7] 孙业赞;于敞;厉松春.铁在铝硅合金中存在的形态及其作用分析[J].铸造,1998(07):42-46.
[8] 杨江波.改善铝硅合金中铁相形态的措施[J].铸造,2000(08):454.
[9] 林小征;印飞;孙宝德.铁对铝硅合金的性能的影响及抵消其有害作用的措施[J].铸造技术,1999(05):29-32.
[10] 陈冰泉,彭军波,缪鄂.稀土、镍、锰对铝硅合金熔敷金属中铁相形态的影响[J].机械工程材料,2003(04):14-17.
[11] 廖恒成,夏锦宏,孙国雄.Sr+B联合熔体处理对Al-Si-Mg合金组织和力学性能的影响[J].中国有色金属学报,2003(01):27-34.
[12] 贾雨,赵平.过共晶铝硅合金中Al-Si-Mn-Fe相的形态影响因素[J].成都理工学院学报,2001(02):214-216.
[13] Li Y J;Lars A.Evolution of primary particles in DC cast AA3003 alloy during heating and homogenization[J].Light Metals,2002:765-770.
[14] F.H.Samuel P.Ouellet .Effect of Mg and Sr Additions on the Formation of Intermetallics in Al-6 Wt Pct Si-3.5 Wt Pct Cu-(0.45) to (0.8) Wt Pct Fe 319-Type Alloys[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1998(12):2871-2884.
[15] 印飞,杨江波,王亦新,王国祥,孙宝德.铝硅合金中针状铁相的断裂现象[J].特种铸造及有色合金,2001(02):1-2.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%