采用扫描电镜原位观测的方法,跟踪观察了低周疲劳载荷下航空用超高强度钢MA250中夹杂物导致裂纹萌生与扩展的微观行为,得到了MA250钢低周疲劳裂纹萌生与扩展的基本特性,讨论了精确测定MA250钢疲劳裂纹扩展速率的方法.
参考文献
| [1] | 李守新.夹杂对高强钢疲劳性能影响的研究[J].中国基础科学,2005(04):14-15. |
| [2] | Murakami Y.Metal Fatigue,Effects of Small and Defects Nonmetallic Inclusions[M].UK:Elservier,2002 |
| [3] | Maropoulos S;Ridley N .Inclumons and Fracture Characteristies of HSLA Steel Forgings[J].Materials Science and Engineering,2004,384A(1-2):64-69. |
| [4] | Z. G. Yang;G. Yao;G. Y. Li .The effect of inclusions on the fatigue behavior of fine-grained high strength 42CrMoVNb[J].International Journal of Fatigue,2004(9):959-966. |
| [5] | 王习术,梁锋,曾燕屏,谢锡善.夹杂物对超高强度钢低周疲劳裂纹萌生及扩展影响的原位观测[J].金属学报,2005(12):1272-1276. |
| [6] | Garrison Jr W M;Moody N R .The Influence of Inclusion Spacing and Microstructure on the Fracture Toughness of the Secondary Hardening Steel AF1410[J].Metallurgical Transactions,1987,18A(07):1257-1263. |
| [7] | Q.Y. Wang;C. Bathias;N. Kawagoishi .Effect of inclusion on subsurface crack initiation and gigacycle fatigue strength[J].International Journal of Fatigue,2002(12):1269-1274. |
| [8] | Barbangelo A .Influence of Nonmetallic Inclusions on Fatigue Crack Growth in a Structural Steel[J].Journal of Materials Science,1985,20(06):2087-2092. |
| [9] | Chapetti M D;Tagawa T;Miyata T .Ultra-Long Cycle Fatigue of High-Strength Carbon Steel Part Ⅰ Review and Analysis of the Mechanism of Failure[J].Materials Science and Engineering,2003,356A(1-2):227-235. |
| [10] | P. J. Laz;B. M. Hillberry .Fatigue life prediction from inclusion initiated cracks[J].International Journal of Fatigue,1998(4):263-270. |
| [11] | Tanaka K;Mura T .A Theory of Fatigue Crack Initiation at Inclusions[J].Metallurgical Transactions,1982,13A(01):117-125. |
| [12] | 张莹,张义文,宋璞生.夹杂物在P/M镍基高温合金中的变形行为及对低周疲劳性能的影响[J].粉末冶金工业,2004(02):1-6. |
| [13] | Denea T;Bretz P L;Tien J K .Inclusion Size Effect on the Fatigue Crack Propagation Mechanism and Fracture Mechanics of a Superalloy[J].Metallurgical Transactions,1992,23A(02):519-526. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%