以压缩膨胀石墨为基体、蔗糖为炭源、磷酸为活化剂,经碳化、活化压片制得膨胀石墨基炭/炭复合电极（EGC电极）。采用低温液氮吸附法和扫描电镜（SEM）进行表征,研究了蔗糖浓度对电极表面结构和孔道特征的影响规律,并以苯酚为处理目标物,考察了不同的电解条件。结果表明,EGC电极以膨胀石墨为骨架,包覆炭膜,孔径主要分布在0.5～2.5nm之间,蔗糖浓度为50%制备的EGC电极比表面积最高,电化学氧化苯酚效果最优。电解苯酚试验中,降低苯酚初始浓度、增加电流密度和电解质浓度有利于提高苯酚的降解效率。
Expanded graphite-based carbon/carbon composite electrode（EGC electrode） had been made of compressed expanded graphite impregnated by sucrose-phosphoric acid solution.The microstructure of the composite electrode had been investigated by nitrogen adsorption method and SEM.The influence of initial sucrose concentration on the surface structure and porous characteristics had been investigated,as well as the impact of electrolytic conditions on phenol degradation.The results indicate that the EGC electrode is comprised of a graphite backbone coated by a thin layer of activated carbon.The pore width distribution is among 0.5-2.5 nm.The EGC electrode could obtain the highest surface areas as the sucrose concentration reaches 50%,and it performs highly effectively in electrochemical oxidation of phenol.The data shows that the removal efficiency of phenol increases with lowering the initial phenol concentration and increasing the current density and electrolyte concentration.
参考文献
| [1] | Fenyun Yi;Shuixia Chen;Chan'e Yuan .Effect of activated carbon fiber anode structure and electrolysis conditions on electrochemical degradation of dye wastewater[J].Journal of hazardous materials,2008(1):79-87. |
| [2] | Oliveira FH;Osugi ME;Paschoal FMM;Profeti D;Olivi P;Zanoni MVB .Electrochemical oxidation of an acid dye by active chlorine generated using Ti/Sn(1-x)Ir O-x(2) electrodes[J].Journal of Applied Electrochemistry,2007(5):583-592. |
| [3] | Zhemin Shen;Wenhua Wang;Jinping Jia .Degradation of dye solution by an activated carbon fiber electrode electrolysis system[J].Journal of hazardous materials,2001(1):107-116. |
| [4] | X.Py;E.Daguerre;D.Menard .Composites of expanded natural graphite and in situ prepared activated carbons[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(8):1255-1265. |
| [5] | Chen X;Zheng YP;Kang F;Shen WC .Preparation and structure analysis of carbon/carbon composite made from phenolic resin impregnation into exfoliated graphite[J].The journal of physics and chemistry of solids,2006(5/6):1141-1144. |
| [6] | 郑春燕,易芬云,陈水挟.活性炭纤维电极法处理含酚废水的研究[J].功能材料,2007(03):451-454. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%