采用快速凝固法制备了Ti53.5Ni22.8Cu23.7合金非晶薄带,研究了长时间热退火对合金条带马氏体相变行为的影响.结果表明,经450~500℃保温退火1~10h条带的相变热滞对保温时间不敏感,约为13~15℃,相变热在4~8J/g之间.随着保温时间延长,500℃退火下的条带相变峰值温度移向高温区而450℃退火下则移向低温区.条带在低于晶化温度的400℃保温10h后晶化程度显著提高,体现出明确的马氏体相变,其相变热滞为13.9℃.合金条带在400℃退火10h形成具有织构(001)的TiCu-B11析出物和Ti2Cu型析出物,在450~500℃退火形成Ti2Cu型析出物.长时间退火下的条带相变特征的差异与退火条带的织构、析出物类型及析出物改变合金基体相的化学成分有关.

参考文献

[1] Otsuka K;Ren X .[J].Progress in Materials Science,2005,50:511-678.
[2] Nam T H;Saburi T;Shimizu K .[J].Materials Transactions JIM,1990,31:959-967.
[3] Furuya Y;Matsumoto M;Kimura H S et al.[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,1991,147:L7-L11.
[4] Nam T H;Saburi T;Nakata Y et al.[J].Materials Transactions JIM,1990,31:1050-1056.
[5] Nam T H;Kim J H;Kim T Y et al.[J].Journal of Materials Science Letters,2002,21:1851-1853.
[6] Nam T H;Park S M;Kim T Y et al.[J].Smart Materials and Structures,2005,14:S239-S244.
[7] Cheng G P;Xie Z L;Liu Y .[J].Journal of Alloys and Compounds,2006,415:182-187.
[8] Kim Y W;Kim H J;Nam T H .[J].Journal of Alloys and Compounds,2008,449:134-138.
[9] Liu Y;Xie Z L;Tong Y X et al.[J].Journal of Alloys and Compounds,2006,415:188-193.
[10] R(o)sner H;Schlo(B)macher P;Shelyakov A V et al.[J].Acta Materialia,2001,49:1541-1548.
[11] Chang S H;Wu S K;Kimura H .[J].INTERMETALLICS,2007,15:233-240.
[12] Lo Y C;Wu S K;Horng H E .[J].ACTA METALLURGICA ET MATERIALIA,1993,41:747-759.
[13] Ishida A;Sato M;Ogawa K et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2006,438-440:683-686.
[14] Sato C;Ledda A;Potapov P et al.[J].Intermetallics,2001,9:395-401.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%