采用提拉法生长了尺寸为φ30 mm × 50 mm的(Yb3+,La3+)∶Gd2SiO5单晶和尺寸为φ24 mm×57 mm的( Yb3+,Tb3)∶GdTaO4单晶,用X射线荧光法测量了掺杂样品的组分浓度在晶体中的分布,拟合了掺杂离子的有效分凝系数,结果表明:Yb3+在Gd2SiO5晶体中的分凝系数为1.185(15),接近单位1,而La3+则为0.68 (10),偏离单位1较多,对晶体的光学均匀性会有较大的影响；Yb3+和Tb3+在GdTaO4中的分凝系数为0.84(14)和0.84(5),接近单位1,对晶体的光学均匀性影响较小.
参考文献
| [1] | Chengfeng Yan;Guangjun Zhao;Lianhan Zhang;Jun Xu;Xiaoying Liang;Du Juan;Wenxue Li;Haifeng Pan;Liangen Ding;Heping Zeng .A new Yb-doped oxyorthosilicate laser crystal: Yb:Gd_2SiO_5[J].Solid State Communications,2006(8):451-455. |
| [2] | 张庆礼,周文龙,刘文鹏,丁丽华,罗建乔,殷绍唐,江海河.Yb3+：GdTaO4的提拉法晶体生长和光谱特性[J].光学学报,2010(03):849-853. |
| [3] | 丁丽华 .新型yb3+激光材料的制备、结构和光谱性能研究[D].北京:中国科学院研究生院,2010. |
| [4] | Liu W P;Zhang Q L;Zhou W L et al.Growth and Luminescence of M-Type GdTaO4 and Tb:GdTaO4 Scintillation Single Crystals[J].IEEE Transactions on Nuclear Science,2010,57(03):1287-1290. |
| [5] | 吴立军,陈万春,粱敬魁.杂质离子在Sr（NO3）2晶体中分凝行为的研究[J].硅酸盐学报,2001(02):163-167. |
| [6] | 赵志伟,姜彦岛.（Yb3+,Nd3+）：Ca3（VO4）2晶体的电荷补偿与分凝系数的关系[J].人工晶体学报,2000(02):143-146. |
| [7] | 徐晓东,赵志伟,宋平新,李抒智,周国清,邓佩珍,徐军.Yb：YAG晶体的晶胞参量及Yb3+分凝系数的研究[J].光子学报,2004(05):567-569. |
| [8] | 张连翰,杭寅,孙敦陆,钱小波,李世锋,殷绍唐,李波,吴柏枚.Nd3+：Y0.5Gd0.5VO4晶体生长和基本特性[J].功能材料与器件学报,2003(02):143-146. |
| [9] | 那木吉拉图,袁兵,阮永丰,袁静.稀土离子在LiYF4晶体中的有效分凝系数[J].硅酸盐学报,2001(06):584-586. |
| [10] | 郭行安.提拉法生长的金绿宝石晶体中Cr3+有效分凝系数的初步测定[J].激光杂志,1985(04):214. |
| [11] | Nicoara I;Pecingina-Garjoaba N;Bunoiu O .Concentration distribution of Yb2+ and Yb3+ ions in YbF3 : CaF2 crystals[J].Journal of Crystal Growth,2008(7/9):1476-1481. |
| [12] | Sun DL;Zhang QL;Wang ZB;Su J;Gu CJ;Wang AH;Yin ST .Concentration distribution of Nd3+ in Nd : Gd3Ga5O12 crystals studied by optical absorption method[J].Crystal Research and Technology: Journal of Experimental and Industrial Crystallography,2005(7):698-702. |
| [13] | ZHANG QingLi,YIN ShaoTang,SUN DunLu,WAN SongMing.Segregation during crystal growth from melt and absorption cross section determination by optical absorption method[J].中国科学G辑(英文版),2008(05):481-491. |
| [14] | 伯廷 E P.X.射线光谱分析的原理和应用[M].纽约-伦敦,Plenum出版社,1975 |
| [15] | 张克从;张乐潓.晶体生长科学与技术[M].北京:科学出版社,1997:411-412. |
| [16] | 闵乃本.晶体生长的物理基础[M].上海:上海科学技术出版社,1982:55. |
| [17] | Larson A C;Von Dreele R B .General Structure Analysis System(GSAS)[R].Los Alamos National Laboratory Report No.LAUR,2004. |
| [18] | Smolin Y I;Tkachev S P .Determination of the Structure of Gadolinium Oxyorthosilicate (Gd2O3) (SiO2)[J].Kristallografiya,1969,14:14-25,ICSDNo27728. |
| [19] | Keller C .üeber Tern(a)are.Oxide des Niobs und Tantls vom Typ ABO4[J].Zeitschrift Fur Anorganische Und Allgemeine Chemie,1962,318(1-2):89-106. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%