The reformation of (Bi,Pb)-2223 from the liquid or melt is very important for a melting process of (Bi,Pb)-2223 tape. By combination of quenching experiment with X-ray diffraction (XRD) analysis, the effect of cooling rate on the evolution of three superconducting phases in the (Bi,Pb)-2223 core of Ag-sheathed tape was investigated. The results show that (Bi,Pb)-2223 reformation from the melt seems to experience different routes during slowly cooling at different rates. One is that (Bi,Pb)-2223 phase reformed directly from the melt, and no Bi-2212 participate in this process. The other is that (Bi,Pb)-2223 is converted from the intermediate product, Bi-2212, which formed from the melt during the first cooling stage. Due to the inherent sluggish formation kinetics of (Bi,Pb)-2223 from Bi-2212, only partial (Bi,Pb)-2223 can finally be reformed with the second route.
参考文献
| [1] | Giannini E.;Savysyuk I.;Garnier V.;Passerini R.;Toulemonde P. Flukiger R. .Reversible melting and equilibrium phase formation of (Bi, Pb)(2)Sr2Ca2Cu3O10+delta[J].Superconductor Science & Technology,2002(11):1577-1586. |
| [2] | Larbalestier D C;Gurevich A;Feldmann D M et al.High-T c superconducting materials for electric power applications[J].Nature,2001,414:368. |
| [3] | Xia S K;Polasek A;Saleh L A et al.Preparation of Bi-2223-Ag tapes by the partial melting route[J].Physica C,2004,408-410:911. |
| [4] | Giannini E.;Passerini R.;Toulemonde P.;Walker E.;Lomello-Tafin M. Sheptyakov D.;Flukiger R. .Bi,Pb(2223) equilibrium and decomposition: in situ high-temperature neutron diffraction study[J].Physica, C. Superconductivity and its applications,2002(Pt.2):895-898. |
| [5] | Li J Y;Soubeyroux L;Zheng H L.[J].Physica C,2006 |
| [6] | Li J Y;Li J G;Zheng H L.The evolution of superconducting phases during melting and reformation of(Bi,Pb)-2223 core in the Ag-sheathed tape[J].Rare metals materials and Engineering,2006 |
| [7] | Lu XY.;Sugawara K.;Kamada S.;Nagata A. .Direct observation of melting and solidification of Bi1.8Pb0.4Sr1.9Ca2.1Cu3.5Ox in various oxygen atmospheres by high-temperature optical microscopy[J].Physica, C. Superconductivity and its applications,2001(1/4):313-320. |
| [8] | Parrell J A;Larbalestier D C;Riley G N et al.Enhancement of the 77 K irreversibility field and critical current density of(Bi,Pb)2Sr2Ca2Cu3Ox tapes by manipulation of the final cooling rate[J].Applied Physics Letters,1996,69(19):2915. |
| [9] | Parrell J.A.;Larbalestier D.C.;Dorris S.E. .Cooling rate effects on the microstructure, critical current density, and T<SUB>c</SUB> transition of one- and two-powder BSCCO-2223 Ag-sheathed tapes[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,1995(2):1275-1278. |
| [10] | Kovac P;Eastell C J;Pachla W .Microstructure and current transport mechanisms in the Bi(2223)/Ag tape[J].Physica C,1997,292:322. |
| [11] | Chen X P;Li M Y;Qu T M et al.Microstructural evolution of Bi-2223/Ag tapes during the cooling process after the first heat treatment[J].Superconductor Science and Technology,2003,16:1162. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%